5982 CMP BIOCLEAN HB silicone antifouling coating is an antifouling coating of the silicone system. Parameters on this page: volume solids 71 ± 2% (ISO 3233), dry film thickness 200 µm, theoretical spreading rate 0.282 L/m². Comparable products from the same brand: 5981B CMP BIOCLEAN PLUS silicone antifouling coating, 5984 CMP BIOCLEAN R silicone antifouling coating, 5986B CMP BIOCLEAN UNDERCOAT PLUS silicone antifouling coating.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5982 CMP BIOCLEAN HB Silicone Antifouling"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 71 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 200 µm |
| Theoretical Spreading Rate | 0.282 L/m2 |
| VOC | 261 g/L (Method 24) |
| Density / Specific Gravity | 1.03 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | SILICON THINNER A, EPOXY THINNER A(… |
| Mixing Ratio | Base : curing agent : accelerator = 75:19:6 (by volume) |
| Colour / Appearance | Light grey |
CMP BIOCLEAN HB is a three-component silicone and antifouling coating.
| Type | Silicone antifouling |
|---|---|
| Use | Used as the topcoat of the CMP BIOCLEAN antifouling system, particularly for vessels on ocean-going routes and fast coastal vessels |
| Mixing Ratio | Base : curing agent : accelerator = 75:19:6 (by volume) |
|---|---|
| Colour | Light grey |
| Flash Point | Base = 34.5°C, hardener = 25.0°C, accelerator = 23°C |
| Density | 1.03 g/ml (ISO: 2811) |
| Volume Solids | 71 ± 2% (ISO: 3233) |
| Volatile organic compound content | 261 g/L (Method 24) |
| Theoretical spreading rate | 0.282 L/m2 |
| Thickness | WFT 282 µm |
| Dry film | 200 µm |
(dry film = 200 µm)
| Temperature | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 7 h | 5 h | 3 h | 2 h | 1 h |
| Hard Dry | 18 h | 12 h | 7 h | 4 h | 2 h | |
| Recoat interval | At least | - | - | - | ||
| At most | - | - | - | |||
| Pot life | 45 min | 30 min | 30 min | |||
| Induction time after mixing | 15 min | 0 min | 0 min | |||
| Minimum launching interval | 40 h | 30 h | 24 h | 18 h | 12 h | |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | 30-85% RH |
| Airless spray: viscosity | - |
| Nozzle | Graco519-721 |
| Paint output pressure | 20 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | SILICON THINNER A, EPOXY THINNER A (for cleaning only) |
| Thinning | 5% (0–5 °C), 3% (6–10 °C), 0% (above 10 °C) by volume, EPOXY THINNER A (for cleaning only) |
| Preceding coat | CMP BIOCLEAN SG |
| Subsequent coat | - |
| Packaging | Three-component |
2. Density, volume solids and volatile organic content are data measured for this product without thinner addition. Values vary according to colour or production process.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.