5981B CMP BIOCLEAN PLUS Silicone Antifouling Paint belongs to Antifouling, Silicone system. CMP BIOCLEAN PLUS is a three-component silicone resin antifouling coating. Parameters on this page: Volume Solids 71 ± 2% (ISO: 3233), Dry Film Thickness 200 µm, Theoretical Spreading Rate 0.282 L/m². Comparable models from the same brand: 5982 CMP BIOCLEAN HB Silicone Antifouling Paint, 5984 CMP BIOCLEAN R Silicone Antifouling Paint, 5986B CMP BIOCLEAN UNDERCOAT PLUS Silicone Antifouling Paint.
Parameter source: CMP original Technical Data Sheet (TDS) “5981B CMP BIOCLEAN PLUS Silicone Antifouling Paint”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 71 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 200 µm |
| Theoretical Spreading Rate | 0.282 L/m2 |
| VOC | 270 g/L (Method 24) |
| Density / Specific Gravity | 1.05 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | SILICON THINNER A |
| Mixing Ratio | Base : curing agent : accelerator = 74.5:16.1:9.4 (by volume) |
| Colour / Appearance | Red-brown, red-brown S |
CMP BIOCLEAN PLUS is a three-component silicone resin antifouling coating.
| Type | Silicone antifouling |
|---|---|
| Use | Used as the topcoat of the CMP BIOCLEAN PLUS system, particularly for ocean-going vessels and fast coastal craft |
| Mixing Ratio | Base : curing agent : accelerator = 74.5:16.1:9.4 (by volume) |
|---|---|
| Colour | Red-brown, red-brown S |
| Flash Point | Base = 26.8 °C, Curing Agent = 26.8 °C, Accelerator = 44.3 °C |
| Density | 1.05 g/mL (ISO: 2811) |
| Volume Solids | 71 ± 2% (ISO: 3233) |
| Volatile organic compound content | 270 g/L (Method 24) |
| Theoretical spreading rate | 0.282 L/m2 |
| Thickness | WFT 282 µm |
| Dry film | 200 µm |
(DFT = 150 µm) drying time
| Temperature | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C |
| Surface Dry | 8 h | 6 h | 4 h | 3 h | 2 h |
| Hard Dry | 19 h | 13 h | 8 h | 5 h | 3 h |
| Recoat interval | Minimum; maximum |
|---|---|
| Pot life | 45 min, 45 min, 30 min, 30 min, 30 min |
| Induction time after mixing | 15 min, 15 min |
| Minimum launching interval | 46 h 36 h 30 h 24 h 18 h |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | 30–85% RH, steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | - |
| Nozzle | Graco519-721 |
| Paint output pressure | 20 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | SILICON THINNER A |
| Thinning | 5% (0–5 °C), 3% (6–10 °C), 0% (above 10 °C) by volume, EPOXY THINNER A (for cleaning only) |
| Preceding coat | CMP BIOCLEAN HB, CMP BIOCLEAN TIECOAT, CMP BIOCLEAN UNDERCOAT PLUS |
| Subsequent coat | - |
| Packaging | Three-component |
Note: 1. Maintain ventilation from application to completion of curing, to remove residual solvent and promote curing.
2. Stir until uniform, then add an appropriate thinner and mix.
3. Generally, thinner is not recommended.
4 Density, volume solids and VOC content are theoretical values calculated without thinner. The values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.