5510B THERMO SHADAN PU Polyurethane Topcoat is a polyurethane coating used as a topcoat. THERMO SHADAN PU is a high-solids topcoat based on acrylic resin and non-yellowing polyisocyanate resin. It has the following advantages: 1. high reflectivity of infrared rays in sunlight. Parameters on this page: volume solids 49 ± 2%; dry film thickness 50 µm; theoretical spreading rate 0.103 L/m². Comparable products from the same brand: 5526 UNY MARINE HS Polyurethane Topcoat, 5526C UNY MARINE HS M Polyurethane Topcoat, 100 EVASIGN No.100 Modified Alkyd Resin Topcoat.
Source: CMP original technical data sheet (TDS) '5510B THERMO SHADAN PU Polyurethane Topcoat'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 49 ± 2% |
|---|---|
| Dry Film Thickness | 50 µm |
| Theoretical Spreading Rate | 0.103 L/m2 |
| VOC | 456 g/L |
| Density / Specific Gravity | 1.26 g/ml |
| Number of Components | Two-component |
| Thinner | URETHANE THINNER A |
| Mixing Ratio | Base : curing agent = 80:20 (by volume) |
| Colour / Appearance | Grey, green |
THERMO SHADAN PU is a high-solids topcoat based on acrylic resin and non-yellowing polyisocyanate resin
It has the following advantages: 1. high reflectivity of infrared rays in sunlight.
2. Good weathering resistance (gloss retention). 3. Good adhesion.
4. Good physical properties such as toughness, impact resistance and abrasion resistance.
5. Good oil and chemical resistance.
| Type | Polyurethane topcoat |
|---|---|
| Use | Can be used as a heat-reflecting paint for the exterior of steel ship superstructures and exposed decks. |
| Mixing Ratio | Base : curing agent = 80:20 (by volume) |
|---|---|
| Colour | Grey, green |
| Flash Point | Base 23 °C, hardener 29.5 °C |
| Density | 1.26 g/ml |
| Volume Solids | 49 ± 2% |
| Volatile organic compound content | 456 g/L |
| Theoretical spreading rate | 0.103 L/m2 |
| Thickness | Wet film 103 µm |
| Dry film | 50 µm |
(dry film 70 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 50 min | 30 min | 20 min | 10 min |
| Hard Dry | 12 h | 8 h | 6 h | 4 h | |
| Recoat interval | At least | 8 h | 6 h | 4 h | 2 h |
At most*
| Pot life | 24 h, 20 h, 16 h, 8 h |
|---|
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 25–35 s (Ford Cup #4) |
| Nozzle | Graco515,615,715,813 |
| Paint output pressure | 11.7-14.7 Mpa |
| Spray gun speed | 80–100 cm/s |
| Thinner | URETHANE THINNER A |
| Thinning | 5–15% by volume |
| Preceding coat | THERMO SHADAN UNDERCOAT EP |
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1. *Refer to the coating specification. 2. VOC content is calculated by formula.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.