100 EVASIGN No.100 Modified Alkyd Resin Topcoat is an alkyd coating used as a topcoat. EVASIGN No.100 is a modified alkyd coating with higher brightness than other ordinary coatings and various colour paints. Parameters on this page: volume solids 53 ± 2%; dry film thickness 40 µm; theoretical spreading rate 0.075 L/m². Comparable products from the same brand: 2400A EVAMARINE Alkyd Topcoat, 2131 ROSWAN QD HB High-build Special Alkyd Primer, 4038G ACRI 700 FINISH G Acrylic Topcoat.
Source: CMP original technical data sheet (TDS) '100 EVASIGN No.100 Modified Alkyd Resin Topcoat (Fluorescent Paint)'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 53 ± 2% |
|---|---|
| Dry Film Thickness | 40 µm |
| Theoretical Spreading Rate | 0.075 L/m2 |
| VOC | 353 g/L |
| Density / Specific Gravity | 1.07 g/ml |
| Number of Components | One-component |
| Flash Point | 40.8°C |
| Thinner | MARINE THINNER |
| Colour / Appearance | Bright red, green, red, orange, lemon yellow, yellow |
EVASIGN No.100 is a modified alkyd coating with higher brightness than other ordinary coatings and various colour paints.
| Type | Modified Alkyd Resin Topcoat (Fluorescent Paint) |
|---|---|
| Use | As a topcoat for safety markings |
| Colour | Bright red, green, red, orange, lemon yellow, yellow |
|---|---|
| Flash Point | 40.8°C |
| Density | 1.07 g/ml |
| Volume Solids | 53 ± 2% |
| Volatile organic compound content | 353 g/L |
| Theoretical spreading rate | 0.075 L/m2 |
| Thickness | Wet film 75 µm |
| Dry film | 40 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1 h | 50 min | 30 min | 20 min |
| Hard Dry | 18 h | 7 h | 4 h | 3 h | |
| Recoat interval | At least | 24 h | 8 h | 2 h | 1.5 h |
At most
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 110 s (Ford cup No.4) |
| Nozzle | Graco615,715 |
| Paint output pressure | 10.7-13.8 Mpa |
| Spray gun speed | 80–100 cm/s |
| Thinner | MARINE THINNER, |
| Thinning | 0–5% by volume |
| Preceding coat | Alkyd white topcoat |
Subsequent coat:
| Packaging | One-component |
|---|
Note: 1 The previous coat must obscure the colour of the substrate.
2 To avoid wrinkling of the film, maintain its weather resistance and achieve the recommended dry film, two coats are recommended.
3 The volatile organic compound content, density and volume solids are theoretical values calculated for a representative colour formulation (bright red) without thinner. Values vary with different colour formulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.