4038G ACRI 700 FINISH G Acrylic Topcoat is an acrylic paint, used as a topcoat. ACRI 700 FINISH G is mainly an acrylic resin-based topcoat, drying by solvent evaporation. Parameters on this page: volume solids 40 ± 2% (ISO: 3233), dry film thickness 40 µm, theoretical spreading rate 0.1 L/m². Comparable products of the same brand: 4038L ACRI 700 FINISH ST Acrylic Topcoat, 100 EVASIGN No.100 Modified Alkyd Resin Topcoat, 2400A EVAMARINE Alkyd Topcoat.
Data source: CMP original Technical Data Sheet (TDS), "4038G ACRI 700 FINISH G Acrylic Topcoat"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 40 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 40 µm |
| Theoretical Spreading Rate | 0.1 L/m2 |
| VOC | 551 g/L (Method 24) |
| Density / Specific Gravity | 1.14 g/ml (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 25.5°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | White (other specified colours) |
ACRI 700 FINISH G is mainly an acrylic resin-based topcoat, drying by solvent evaporation.
It has good adhesion, weathering resistance and colour/gloss retention.
| Type | Acrylic Topcoat |
|---|---|
| Use | A topcoat for ship freeboard and superstructures |
| Colour | White (other specified colours) |
|---|---|
| Flash Point | 25.5°C |
| Density | 1.14 g/ml (ISO: 2811) |
| Volume Solids | 40 ± 2% (ISO: 3233) |
| Volatile organic compound content | 551 g/L (Method 24) |
| Theoretical spreading rate | 0.1 L/m2 |
| Thickness | Wet film 100 µm |
| Thickness | Dry film 40 µm |
(dry film 40 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1.5 h | 1 h | 30 min | |
| Hard Dry | 10 h | 8 h | 6 h | 4 h | |
| Recoat interval | At least | 16 h | 12 h | 8 h | 6 h |
At most
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 60 seconds (Ford Cup No. 4) |
| Nozzle | Graco719 |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | BANNOH 500,BANNOH 200,BISCON HB-NT L,ACRI 700 PRIMER G |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir the base with a stirrer until uniform, then add the curing agent and mix with a powerful stirrer. Finally add an appropriate thinner and mix.
3 Density and VOC content are theoretical calculated values based on a representative colour formulation (white) excluding thinner. The values vary depending on the formulation of different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.