4037J ACRI 700 PRIMER J Acrylic Anti-corrosive Primer is an acrylic paint for use as a primer. ACRI 700 PRIMER J is a high-performance anti-corrosive primer based mainly on an acrylic resin topcoat and drying by solvent evaporation. Parameters on this page: volume solids 43 ± 2%, theoretical spreading rate 0.093–0.186 L/m², number of components one-component. Comparable products of the same brand: 9102 SEAJET 015 acrylic resin primer, 1050 NZ PRIMER S zinc-free epoxy shop primer, 200 GALVANITE No.200 PRIMER epoxy galvanized steel primer.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "4037J ACRI 700 PRIMER J Acrylic Anti-corrosive Primer"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 43 ± 2% |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 0.093-0.186 L/m2 |
| VOC | 492 g/L |
| Density / Specific Gravity | 1.23 g/ml |
| Number of Components | One-component |
| Flash Point | 24.0°C |
| Thinner | CR/ACRI THINNER C |
| Colour / Appearance | Light grey, red-brown, white |
ACRI 700 PRIMER J is a high-performance anti-corrosive primer based mainly on an acrylic resin topcoat and drying by solvent evaporation. It can be applied directly to bare steel or to existing coating surfaces such as acrylic, chlorinated rubber and epoxy. It offers good application properties, and high film thickness can be achieved particularly by spray application.
| Type | Acrylic anti-corrosive primer |
|---|---|
| Use | Anti-corrosive primer for exposed areas |
| Colour | Light grey, red-brown, white |
|---|---|
| Flash Point | 24.0°C |
| Density | 1.23 g/ml |
| Volume Solids | 43 ± 2% |
| Volatile organic compound content | 492 g/L |
| Theoretical spreading rate | 0.093-0.186 L/m2 |
| Thickness | Wet film 93–186 µm |
| Dry film 40–80 | µm |
(dry film 60 µm)
| Temperature | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 2 h | 1.5 h | 1.2 h | 1 h | 30 min |
| Hard Dry | 10 h | 8 h | 7 h | 6 h | 4 h | |
| Recoat interval | At least | 12 h | 10 h | 8 h | 7 h | 5 h |
At most
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 120 s (Ford cup #4) |
| Nozzle | Graco721,723 |
| Paint output pressure | 11.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER C |
| Thinning | 0–7% by volume |
| Preceding coat | Such as NZ PRIMER, EPICON ZINC RICH PRIMER and CERABOND |
| Subsequent coat | ACRI 700 FINISH J |
| Packaging | One-component |
Note: 1. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
2 Excessive thinner will reduce anti-sagging performance.
3 Density, volume solids and volatile organic content are based on a representative colour formulation (light grey) without thinner.
Values may vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.