ZINDN Water-borne Cold-spray Zinc ZD96-6 Two-component is a cold galvanizing coating in the water-borne system. Used for long-term anticorrosive protection of steel; can be used as a single coat, or overcoated with a compatible heavy-duty anticorrosive coating for synergistic effect to meet various protection requirements. A two-component, high-solids heavy-duty anticorrosive coating composed of water-borne modified fusing agent, zinc powder, water and additives. Parameters on this page: volume solids 60 ± 3%; dry film thickness 40/60/80 µm; theoretical spreading rate 0.453 kg/m². Comparable products from the same brand: ZDW6810-Z1550 Water-borne Cold-spray Graphene Zinc Coating, Water-borne High-performance Antifouling Topcoat ZDW3052, ZINDN Self-spray Zinc Aluminium ZD18-16.
Source: ZINDN original technical data sheet (TDS) 'ZINDN Water-borne Cold-spray Zinc ZD96-6 Two-component'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 3% |
|---|---|
| Dry Film Thickness | 40/60/80 µm |
| Theoretical Spreading Rate | 0.453 kg/m² |
| VOC | — |
| Density / Specific Gravity | 3.4 ± 0.1 |
| Number of Components | Two-component |
| Flash Point | >95°C |
| Thinner | Pure water (clean tools before the paint is touch dry; once touch dry, a glycol ether solvent may be used for tool… |
| Mixing Ratio | Component A (liquid) : Component B (powder) = 1:5 |
ZD96-6 ZINDN Water-borne Cold-spray Zinc
A two-component, high-solids heavy-duty anticorrosive coating composed of water-borne modified fusing agent, zinc powder, water and additives.
ZINDN Water-borne Cold-spray Zinc can apply, at normal temperature, a zinc protective layer with a zinc content above 92%, with high anticorrosive performance;
Excellent weather resistance;
Strong adhesion and good recoatability;
Convenient application, low VOC content, safe and environmentally friendly.
For long-term anti-corrosion of steel; may be used as a single coat, or overcoated with a compatible heavy-duty coating to provide synergistic protection meeting various protective requirements. An ideal material to replace or repair hot-sprayed zinc and hot-dip galvanised coatings.
| Colour | Zinc grey |
|---|---|
| Gloss | Matt |
| Volume Solids | 60±3% |
| Density (kg/L) | 3.4±0.1 |
| Dry film thickness (µm) | Minimum 40 | Typical 60 | Maximum 80 |
| Wet film thickness (µm) | 66.7 | 100 | 133.4 |
| Theoretical spreading rate (kg/m²) | 0.226 | 0.34 | 0.453 |
| Practical Spreading Rate | Allowing for a suitable loss factor |
|---|
| New steel | Remove grease from the surface with a suitable cleaner, and rinse off salts and other contaminants with fresh water. Remove weld slag, and grind welds and sharp edges smooth. Abrasive blast clean to Sa 2.5 (ISO 8501-1); the ideal surface roughness is Rz 40–75 µm (medium roughness on the ISO 8503-1 comparator). Apply the primer within 4 hours of blast cleaning. |
|---|---|
| Repair of galvanised surfaces | Thoroughly remove grease from the surface with a suitable cleaner, wash off salts and other contaminants with high-pressure fresh water, grind small rusted areas with power tools, and touch up with this product. |
Application ambient temperature 5–50 °C, relative humidity not above 80%, and the steel surface temperature at least 3 °C above the dew point; outdoor use is prohibited in bad weather such as rain, fog, snow, strong wind and heavy dust;
In hot summer weather, guard against dry spray; provide ample ventilation during application and drying in confined spaces;
The product is supplied as a unit in two cans. Slowly add the zinc dust pigment to the liquid component and stir continuously until uniform. Then strain through a 60–80 mesh sieve before use. During use, stir the mixed coating continuously to prevent zinc dust settling. Once mixed, it shall be used within the specified pot life.
| Mixing ratio (by weight) | Component A (liquid) : Component B (powder) = 1:5 |
|---|---|
| Thinner / Cleaning Solvent | Pure water (clean tools before the paint is touch dry; once touch dry, a glycol ether solvent may be used for tool cleaning) |
| Application Methods | Airless spray and air spray are recommended; brush and roller are recommended only for touch-up, small-area application or repair. |
|---|
| Application Methods | Unit | High-pressure airless spray | Air Spray | Brush/roller |
| Spray gun tip size | mm | 0.38~0.48 | 1.5~2.0 | —— |
| Spray pressure | kg/cm² | 150~200 | 3~4 | —— |
| Thinning quantity | % | 0~3 | 2~8 | 0~5 |
| Substrate surface temperature | 5°C | 15°C | 25°C | 35°C |
| Surface Dry | 2 h | 1 h | 30 min | 20 min |
| Hard Dry | 10 h | 8 h | 4 h | 2 h |
Minimum self-recoat interval
5 h; 4 h; 2 h; 1 h
interval
Minimum recoat over sealer
36 h; 24 h; 18 h; 12 h
Interval
| Maximum recoat interval | Unlimited. Before applying the next coat, the surface should be clean, dry and free of zinc salts and contaminants. Note: the above data were measured under good ventilation, typical film thickness and 65% relative humidity, for reference only. |
|---|
Actual drying times and the interval before recoating may be longer or shorter depending on film thickness, ventilation, humidity, the underlying paint, requirements for early handling and mechanical strength, and other factors.
| Preceding coat | Apply directly to steel surfaces prepared to Sa 2.5, or to hot-dip galvanized and thermally sprayed zinc surfaces; |
|---|---|
| Subsequent coat | ZINDN water-borne epoxy sealer. |
| Packaging Specifications | Component A 4 kg, component B 20 kg |
|---|---|
| Flash Point | >95°C |
| Storage conditions | Store in accordance with national regulations. Keep at a temperature above 0 °C in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. |
| Shelf life | Shelf life is 6 months under good storage conditions. |
Site safety must comply with the relevant national or local regulations. Read the safety labels on the packaging and the product Safety Data Sheet (MSDS).
Avoid inhaling spray mist, avoid skin and eye contact with the paint, never swallow this product, and take necessary precautions for fire, explosion and environmental protection. Use in a well-ventilated area. In narrow or poorly ventilated areas, provide strong ventilation to aid film drying and curing.
Waste disposal must comply with the relevant national or local regulations.
The information and data in this document are accumulated from our tests and practical experience and may serve as an application guide. Since the use of the product is generally beyond our control, we guarantee only the quality of the product itself. We reserve the right to modify this document without prior notice as the product is improved.
| Version information | Published in June 2022; this data sheet supersedes all previous versions |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.