Megafiller Deck Luxury Yacht Deck Filler belongs to auxiliary. This product requires sealing with a full coat of Megayacht Epoxy Primer prior to application of teak planking. Suitable for surfaces primed with pre-treatment primer on carbon steel, aluminium, composite and wood substrates. Parameters on this page: volume solids 100%, number of components two-component. Comparable models from the same brand: Jota Alfa Additive, Jota Fulfill 100 Unsaturated Polyester Fairing Compound, Jotatherm CSP1 Scrim Low-Temperature Spill Protection Coating Reinforcement Mesh.
Parameter source: JOTUN original technical data sheet (TDS) “Megafiller Deck Luxury Yacht Deck Filler”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% |
|---|---|
| Dry Film Thickness | — |
| Theoretical Spreading Rate | — |
| VOC | 88g/kg |
| Density / Specific Gravity | 0.57 kg/L |
| Number of Components | Two-component |
| Flash Point | 130 °C |
| Shelf life | 36 months : 36 months |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Luxury Yacht Deck Filler (467)
This is a two-component epoxy fairing compound/filler. Ultra-light, solvent-free product. Excellent sanding properties, strong adhesion, low shrinkage. Suitable for surfaces primed with pre-treatment primer on carbon steel, aluminium, composite and wood substrates.
In deck areas below the teak deck surface. Level the chamfers on metal or composite substrate surfaces with a trowel or fairing board. This product requires sealing with a full coat of Megayacht Epoxy Primer prior to application of teak planking.
Others
Light brown (after mixing brown Component A and white Component B)
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 100% |
| Flash Point | ISO 3679 Method 1 | 130 °C |
| density | Theoretical Value | 0.57 kg/L |
| VOC (Volatile Organic Compounds) solvent emission guidance | SED (1999/13/EC) | 88g/kg |
The data listed are based on factory batch production and may vary slightly with colour.
All data apply to the mixed paint only.
| Film Thickness and Spreading Rate | Dry Film Thickness | Wet Film Thickness | Theoretical Spreading Rate |
| (µm) | (m²/L) | ||
| Minimum | 1000 | 1 | |
| Maximum | 32000 | 0.03 | |
| Typical | 10000 | 0.1 | |
To minimize dry film shrinkage stress, application in accordance with the typical dry film thickness is recommended.
For details, consult your local JOTUN office.
To ensure lasting adhesion of the next coat, all surfaces must be clean, dry and free of contaminants.
Surface Preparation
| Substrate | Minimum | Recommended | |
| Coated surfaces New Megacote or Megaprimer: | New Megacote or Megaprimer: | ||
| Clean, dry and intact compatible primer (compliant with ISO | Clean, dry and intact compatible primer (compliant with ISO | ||
| 12944-4 | clause 6.1). | 12944-4 | clause 6.1). |
| Remove various contaminants that may affect the adhesion of the intermediate coat. | Remove various contaminants that may affect the adhesion of the intermediate coat. | ||
| Cured Megacote or Megaprimer: | Cured Megacote or Megaprimer: | ||
| If the maximum overcoating interval is exceeded, cleaning, | If the maximum overcoating interval is exceeded, cleaning, | ||
| abrading with P150–P180 aluminium oxide or silicon carbide paper | abrading with P150–P180 aluminium oxide or silicon carbide paper | ||
| by hand or power tool, or applying another coating, | by hand or power tool, or applying another coating, | ||
| depending on the situation. | depending on the situation. |
This product may be applied by the following methods
| Trowel | Use a putty knife, pocket knife, fairing board or other suitable tools. |
|---|
Mix the two components thoroughly until a uniform colour is obtained. Mix with a trowel or an approved filler mixer.
| Luxury Yacht Deck Filler, Component A | 1 part |
| Megafiller Deck Comp B | 1 part |
Do not add thinner.
| Cleaner | JOTUN Thinner No. 17 |
|---|
| Substrate Temperature | 10 °C | 23 °C | 35 °C |
| Touch Dry | 24 h | 16 h | 4 h |
| Walk-on Dry | 72 h | 18 h | 12 h |
| Minimum recoat interval | 12 h | 8 h | 2 h |
| Dry/cured to service | 14 days | 7 days | 3 days |
Drying and curing times are based on the stated film thickness range, measured in a controlled laboratory environment at below 85% relative humidity.
| Touch Dry | Condition in which light finger pressure leaves no fingerprint or adhesion. Dry sand scattered on the surface can be brushed off without adhesion or damage to the surface. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Maximum overcoating interval, atmospheric environment: the maximum time within which the next coat can be applied without any surface preparation.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 30 min |
The following Shore hardness values are measured in accordance with ISO 868 after the product has fully cured, at an average dry film thickness of 1000 µm and 14 days curing at 20 °C.
| No sanding | Tested immediately after 1 s: 41 ± 5 | Tested after 3 s: 31 ± 5 | Tested after 15 s: 27 ± 5 |
| Sanded with P180 abrasive paper | 43± 5 | 33± 5 | 26± 5 |
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 120°C | 120 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy |
| Subsequent coat: | Epoxy |
Instructions for use:
Before sealing with Megacote, the high-density epoxy fairing filler Megafiller Smooth may be applied to depressions and pinholes on the coated surface to achieve the desired result.
| Volume | Container Size | |
| (L) | ||
| Luxury Yacht Deck Filler, Component A | 10 / 200 | 12 / 219 |
| Megafiller Deck Comp B | 12 / 219 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Luxury Yacht Deck Filler, Component A | 36 months |
| Megafiller Deck Comp B | 36 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge.
Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
Products used primarily as primers and antifouling paints may show slight colour variation from batch to batch. Such products may chalk and fade when exposed to sunlight and weathering.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.