Suitable for carrying various corrosive cargoes, e.g. solvents (including methanol), chemicals, refined and crude petroleum products, vegetable oils and animal oils. A two-component epoxy cargo oil tank coating. Parameters on this page: volume solids 48% ± 2%; dry film thickness 90 µm; theoretical spreading rate 5.33 m²/L. Comparable products from the same brand: Interbond 201 - Low Temperature Epoxy Primer/Topcoat, Intercryl 559 Smooth Wash-resistant Topcoat, Intergard 7020 Abrasion-resistant Aluminium Pure Epoxy.
Source: INTERNATIONAL original technical data sheet (TDS) 'Interline 904 Epoxy Cargo Oil Tank Coating'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 48% ± 2% |
|---|---|
| Dry Film Thickness | 90 µm |
| Theoretical Spreading Rate | 5.33 m²/L |
| VOC | 497 g/L (as supplied) (EPA Method 24); 387 g/kg (… |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Mixing Ratio | Component A : Component B = 6.30:1 (by volume) |
| Colour / Appearance | TCA932 pink, TCA933 pale yellow, TCA934 grey |
| Gloss | Semi-gloss |
The manufacturer's datasheet for this model does not state the coating position or resin type, so it has not been assigned to the above categories. Browse similar products by category, orContact Usconfirm the coating system.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
A two-component epoxy cargo oil tank coating.
Suitable for carrying various corrosive cargoes, e.g. solvents (including methanol), chemicals, refined and crude petroleum products, vegetable oils and animal oils.
For newbuilding or maintenance and repair.
| Colour | TCA932 pink, TCA933 pale yellow, TCA934 grey |
|---|---|
| Topcoat/gloss | Semi-gloss |
| Component B (curing agent) | TCA935 |
| Volume Solids | 48% ±2% (ISO 3233:1998) |
| Mixing ratio | Component A : Component B = 6.30:1 (by volume) |
| Standard film thickness | 90 µm dry film thickness (188 µm wet film thickness) |
| Theoretical Spreading Rate | At 90 µm dry film thickness, the theoretical spreading rate is 5.33 m²/L, allowing an appropriate loss factor |
| Application Methods | Airless spray, roller, brush |
| Flash Point | Component A 23 °C; component B 38 °C; after mixing 31 °C |
| Induction Time | Not required |
| Drying data | 5°C | 10°C | 25°C | 35°C |
| Touch dry [ISO 9117/3:2010] | 8 h | 6 h | 3 h | 90 min |
| Hard dry [ISO 9117-1:2009] | 18 h | 14 h | 7 h | 4 h |
| Pot life after mixing | 5 h | 4 h | 3.5 h | 1.5 h |
| Recoat data — see the “Limitations” section | Substrate Temperature | |||||||
| 5°C | 10°C | 25°C | 35°C | |||||
| When recoating the following products | Minimum | Maximum | Minimum | Maximum | Minimum | Maximum | Minimum | Maximum |
| Interline 904 | 36 h | 35 days | 30 h | 34 days | 16 h | 28 days | 12 h | 14 days |
| Volatile Organic Compounds | 497 g/L (as supplied) (EPA Method 24); 387 g/kg (as supplied liquid paint). EU Solvent Emissions Directive (Commission Directive 1999/13/EC). VOC values are typical values provided for reference only. They may vary with factors such as colour and normal manufacturing tolerance. |
|---|
When used as part of an approved scheme, this coating holds the following certificates: • Food contact - grain loading (NOHA). For details, consult the local International Paint representative.
For the paint system best suited to the surface to be protected, consult your local International Paint representative.
For cargo oil tanks or slop tanks, refer to the Interline 904 cargo oil tank or slop tank application procedure.
Applied in accordance with the standard Worldwide Marine Specifications.
All surfaces to be coated must be clean, dry and free of contaminants.
Wash with high-pressure or ordinary fresh water as appropriate, and remove all oil, grease, soluble contaminants and other foreign matter in accordance with the SSPC-SP1 solvent cleaning standard.
Newbuilding/major repair: where required, remove weld spatter and grind welds and sharp edges smooth.
Abrasive blast-clean to Sa 2.5 (ISO 8501-1:2007). If oxidation occurs between blasting and application of Interline 904, re-blast the surface to the specified pictorial standard.
Surface defects exposed during blasting must be ground, welded or treated by a suitable method.
For maintenance, consult International Paint.
For specific advice, consult your local International Paint representative.
Note: for the marine environment in North America, the following surface preparation standard may be used: SSPC-SP10 in place of Sa 2.5 (ISO 8501-1:2007)
The coating is supplied in two containers as one unit. Always mix the entire unit in the supplied ratio.
(1) Stir the base (Component A) with a power mixer.
(2) Mix all of the curing agent (Component B) with the base (Component A) and stir thoroughly with a power mixer.
Not recommended. Use International GTA713 only in special cases (max 5% by volume). Thinning must not exceed the range allowed by local environmental regulations.
Recommended nozzle tip size 0.46–0.58 mm (18–23 thou); total fluid pressure at the nozzle not less than 176 kg/cm² (2500 psi)
Conventional spray application is not recommended.
Brush application is recommended for small areas only. Several coats may be required to achieve the specified film thickness.
Roller application is recommended for small areas only. Several coats may be required to achieve the specified film thickness.
International GTA713
Do not leave paint in the hose, spray gun or spray equipment. Flush all equipment thoroughly with International GTA713. Once a set is mixed, it should not be resealed; if the work interruption is too long, re-mix fresh components before resuming.
Clean all equipment with International GTA713 immediately after use. Flushing spray equipment periodically during the day is good practice. Cleaning frequency depends on spray volume, temperature and usage time (including interruptions). Do not exceed the pot life of the mixed paint.
All surplus paint and empty containers must be disposed of in accordance with appropriate local regulations/laws.
If welding or flame cutting is performed on metal coated with this product, dust and fumes will be released; use suitable personal protective equipment and local exhaust ventilation. In North America, follow the instructions in ANSI/ASC Z49.1 “Safety in Welding and Cutting”.
All work related to the application and use of this product must comply with national health, safety and environmental protection standards and regulations.
Before using this product, obtain, read and follow the health and safety information in the Material Safety Data Sheet for the product. Read and observe all precautions in the Material Safety Data Sheet and on the container label. If these warnings and requirements are not fully understood, or cannot be strictly observed, do not use the product. During application and drying of the product, provide adequate ventilation and protective measures to keep solvent vapour concentrations within safe limits, so as to prevent poisoning or oxygen deficiency. Take protective measures to avoid skin and eye contact with the product (e.g. gloves, goggles, face shield, barrier cream). Specific safety measures depend on the application method and working environment.
Emergency contact: USA/Canada — medical 1-800-854-6813; Europe — tel. (44) 191 4696111, hospital and doctor (44) 207 6359191; other regions — contact the regional office
Consult International Paint to confirm the suitability of Interline 904 for the cargo to be carried.
Drying times and overcoating intervals may vary with site factors such as tank geometry and ventilation rate.
Recoat data are for guidance only and depend on local climatic and environmental conditions. For specific advice, consult your local International Paint representative.
Apply in good weather. The temperature of the surface to be coated must be at least 3 °C above the dew point. Unless otherwise specifically instructed, raise the paint temperature to between 21 and 27 °C before mixing and application to achieve optimum application performance. Unmixed paint (in sealed containers) must be stored protectively as specified in the Storage section of this product data sheet. The technical and application data given here are intended as general guidance for establishing an application procedure. Test results are obtained in a controlled laboratory environment, and International Paint does not claim that the published test results, or any other test results, accurately represent results obtained in all site environments. Because application, environmental and design parameters vary widely, care must be exercised in coating selection, performance verification and use.
| Packaging Specifications | Component A | Component B | ||
| Volume | Packaging | Volume | Packaging | |
| 20 L | 17.25 L | 20 L | 2.75 L | 3 L |
For other packaging sizes, consult International Paint.
| Packaging Specifications | Packaging weight |
|---|---|
| 20 L | 29.49 kg |
| Shelf life | At 25 °C, minimum 12 months. Thereafter, re-inspection is required. Store in a dry, sheltered place away from heat and sources of ignition. |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.