9050 BONDET PUTTY Epoxy Polyamide Putty is an epoxy coating. BONDET PUTTY is a putty composed of epoxy resin and polyamide resin as the base; in addition to physical properties such as excellent adhesion, impact resistance and abrasion resistance, it also has chemical properties such as salt water resistance, oil resistance, alkali resistance and dilute acid resistance, making it especially suitable as a putty for tank interiors and underwater parts of ship hulls. Parameters on this page: volume solids 100%, dry film thickness 2000 µm, theoretical spreading rate 2 L/m². Comparable models from the same brand: 5006 ALP 500 epoxy, 5055 BANNOH 500 epoxy, 5055D BANNOH 500 AC epoxy.
Parameter source: CMP original technical data sheet (TDS) for 9050 BONDET PUTTY Epoxy Polyamide Putty; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% |
|---|---|
| Dry Film Thickness | 2000 µm |
| Theoretical Spreading Rate | 2 L/m2 |
| VOC | 0 g/L (theoretical) |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A (for cleaning) |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
| Colour / Appearance | Grey |
BONDET PUTTY is a putty composed of epoxy resin and polyamide resin as the base; in addition to physical properties such as excellent adhesion, impact resistance and abrasion resistance, it also has chemical properties such as salt water resistance, oil resistance, alkali resistance and dilute acid resistance, making it especially suitable as a putty for tank interiors and underwater parts of ship hulls.
| Type | Epoxy polyamide putty |
|---|---|
| Use | Applied around anodes as an anti-corrosion coating, or used to apply, fill and repair gaps and small holes in ship hull shells and tank interiors. |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | - |
| Volume Solids | 100% |
| Volatile organic compound content | 0 g/L (theoretical) |
| Theoretical spreading rate | 2 L/m2 |
| Wet Film Thickness | 2000 µm |
| Dry Film Thickness | 2000 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 7 h | 5 h | 3 h | 2 min |
| Hard Dry | 26 h | 18 h | 8 h | 5 h | |
| Recoat interval | At least | 14 h | 10 h | 6 h | 4 h |
| At most | 10 days | 7 days | 4 days | 2 days | |
| Pot life | 8 h | 6 h | 3 h | 2 h |
| Application method | Trowel application |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Thinner | EPOXY THINNER A (for cleaning) |
| Thinning | - by volume |
The entire surface should be clean, dry and free from any contaminants.
| Remove damaged areas by abrasive blasting to at least Sa 2½ (ISO 8501-1 | 2007); mechanical cleaning methods are also acceptable. |
|---|
It can be applied over epoxy primer.
| Preceding coat | - |
|---|---|
| Subsequent coat | Epoxy resin coating |
| Packaging | Two-component |
Note: 1. In the mixing ratio above, thoroughly knead the base and curing agent until the colour becomes uniform.
2. Volume solids and volatile organic compound content are calculated values based on the formula.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.