5055D BANNOH 500 AC Epoxy Paint is an epoxy paint. It has good adhesion, a tough film, abrasion resistance and many other physical properties. It also offers wide applicability, seawater corrosion resistance and resistance to the adverse effects of cathodic protection on the coating film. Parameters on this page: volume solids 60 ± 2% (ISO: 3233), dry film thickness 100–200 µm, theoretical spreading rate 0.167–0.333 L/m². Comparable products of the same brand and type: 5006 ALP 500 Epoxy Paint, 5055 BANNOH 500 Epoxy Paint, 5056 BANNOH 500 QD Epoxy Paint.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "5055D BANNOH 500 AC Epoxy Paint"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.167-0.333 L/m2 |
| VOC | 376 g/L (Method 24) |
| Density / Specific Gravity | 1.30 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
| Colour / Appearance | Grey, red-brown |
BANNOH 500 AC is a universal primer. It has good adhesion, a tough film, abrasion resistance and many other physical properties.
And has excellent applicability, resisting seawater corrosion and the adverse effects of cathodic protection on the film.
It is suitable for spraying on many areas of the hull.
| Type | Epoxy |
|---|---|
| Use | Used as an anti-corrosion epoxy primer for various buildings, steel structures, tank surfaces and ship hulls. |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
|---|---|
| Colour | Grey, red-brown |
| Flash Point | Base 23.1°C, Hardener 24.9°C |
| Density | 1.30 g/mL (ISO: 2811) |
| Volume Solids | 60 ± 2% (ISO: 3233) |
| Volatile organic compound content | 376 g/L (Method 24) |
| Theoretical spreading rate | 0.167-0.333 L/m2 |
| Thickness | Wet film 167–333 µm |
| Dry film | 100–200 µm |
(dry film 200 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 7 h | 5.5 h | 4 h | 2.5 h |
| Hard Dry | 24 h | 18 h | 10 h | 8 h | |
| Recoat interval | At least | 24 h | 18 h | 10 h | 8 h |
At most*
| Pot life | 18 h, 14 h, 7 h, 4 h |
|---|
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.6-2.0Pa.s |
| Nozzle | (Graco)623,621 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
If applied directly to steel surfaces, surface preparation to ISO Sa2½ is required; if overcoated on a primer, surface preparation to ISO St3 is required
| Preceding coat | CERABOND, EPICON ZINC RICH PRIMER B-2, EPICON ZINC HB-2 SH and others |
|---|---|
| Subsequent coat | BANNOH 500 N, BANNOH 500 AC, EPICON FINISH HB, UNY MARINE HS and others |
| Packaging | Two-component |
Note: 1. *Result obtained in consultation with the CMP sales department. 2. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
3 Density, volume solids content and volatile organic content are theoretical calculated values excluding thinner. The values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.