5055 BANNOH 500 Epoxy Coating belongs to the epoxy coatings category. It offers good adhesion, a tough film, abrasion resistance and many other physical properties. It also provides excellent applicability, resistance to seawater corrosion and resistance to the adverse effects of cathodic protection on the film. Parameters on this page: volume solids 63 ± 2%, dry film thickness 100–200 µm, theoretical spreading rate 0.16–0.32 L/m². Comparable products of the same brand and type: 5006 ALP 500 Epoxy Coating, 5055D BANNOH 500 AC Epoxy Coating, 5056 BANNOH 500 QD Epoxy Coating.
Parameter source: manufacturer's Technical Data Sheet (TDS) "5055 BANNOH 500 Epoxy Coating" from CMP; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 63 ± 2% |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.16-0.32 L/m2 |
| VOC | 401g/L |
| Density / Specific Gravity | 1.31 g/mL |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Light grey, grey, red-brown |
LHUGOKUMARINE PAINTS,LTD BANNOH 500 is an all-purpose primer. It offers good adhesion, a tough film, abrasion resistance and many other physical properties.
And has excellent applicability, resisting seawater corrosion and the adverse effects of cathodic protection on the film.
It is suitable for spraying on many areas of the hull.
| Type | Epoxy |
|---|---|
| Use | For corrosion protection of ship hulls, superstructures, external decks and ballast water tanks |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Light grey, grey, red-brown |
| Flash Point | Base 23.1 °C, curing agent 24.9 °C |
| Density | 1.31 g/mL |
| Volume Solids | 63±2% |
| Volatile organic compound content | 401g/L |
| Theoretical spreading rate | 0.16-0.32 L/m2 |
| Thickness | WFT 159–317 µm |
| Dry film | 100–200 µm |
(dry film 200 µm)
| Temperature | 5°C | 10°C | 20°C | 30°C | |
| Drying Time | Surface Dry | 7 h | 5.5 h | 4 h | 2.5 h |
| Hard Dry | 24 h | 18 h | 10 h | 8 h | |
| Coating interval | At least | 24 h | 18 h | 10 h | 8 h |
At most*
| Pot life | 18 h 14 h 7 h 4 h |
|---|
Application methods: airless spray, brush
| Weather: temperature | Minimum 5 °C |
|---|---|
| Humidity | Maximum 85% RH |
| Apply by airless spray | Viscosity: 1.6–2 Pa·s |
| Nozzle | (Graco) 623,621 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | CERABOND, EPICON ZINC RICH PRIMER and other similar products |
| Subsequent coat | BANNOH 500 N,BANNOH 500 AC,SILVER SQ-K.M,EPICON FINISH HB |
| Packaging | Two-component |
Note: 1* Result obtained in consultation with the CMP sales department. 2 Ventilation equipment is necessary, such as in enclosed spaces or confined spaces under low-temperature conditions, to remove evaporated solvent during application and film formation and to promote paint film formation.
| 3 | Waiting time before loading the first cargo |
|---|
| Temperature | 10°C | 20°C | 30°C |
| (days) | 18 | 10 | 6 |
| 4 | VOC content is a theoretical calculated value |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.