8340A SILVA SPAR Alkyd Aluminium Paint belongs to alkyd coatings. SILVA SPAR is a coating composed of an oil-based resin as binder combined with aluminium paste. Parameters on this page: volume solids 45 ± 2%, dry film thickness 15–25 µm, theoretical spreading rate 0.033–0.056 L/m². Comparable models from the same brand: 100 EVASIGN No.100 Modified Alkyd Resin Topcoat, 2131 ROSWAN QD HB High-build Special Alkyd Primer, 2400A EVAMARINE Alkyd Topcoat.
Parameter source: CMP original technical data sheet (TDS) “8340A SILVA SPAR Alkyd Aluminium Paint”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 45 ± 2% |
|---|---|
| Dry Film Thickness | 15–25 µm |
| Theoretical Spreading Rate | 0.033-0.056 L/m2 |
| VOC | 440 g/L |
| Density / Specific Gravity | 1.00 g/mL |
| Number of Components | One-component |
| Flash Point | 28.8°C |
| Thinner | MARINE THINNER |
| Colour / Appearance | Silver |
SILVA SPAR is a coating composed of an oil-based resin as binder combined with aluminium paste.
1. Smooth surface, high gloss, resistant to dust accumulation.
2. Strong effect of reflected light.
3. Good corrosion resistance.
4. Excellent coating performance.
5. Excellent heat resistance.
| Type | Alkyd Aluminium |
|---|---|
| Use | Aluminium-pigmented topcoat. Suitable as a topcoat in ship holds (cargo holds) up to 150 °C. |
| Colour | Silver |
|---|---|
| Flash Point | 28.8°C |
| Density | 1.00 g/mL |
| Volume Solids | 45 ± 2% |
| Volatile organic compound content | 440 g/L |
| Theoretical spreading rate | 0.033-0.056 L/m2 |
| Wet Film Thickness | 33–56 µm |
| Dry Film Thickness | 15–25 µm |
Drying time, overcoating interval
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C |
| Surface Dry | 4 h | 2 h | 1 h | 30 min |
| Hard Dry | 18 h | 12 h | 6 h | 3 h |
| At least | 30 h | 24 h | 15 h | 10 h |
| At most | - | |||
| Application method | Airless Spray, Brush |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 33 s (Ford Cup #4) |
| Nozzle | Graco 713,715 |
| Paint output pressure | 10.7-13.8 Mpa |
| Spray gun speed | 80–100 cm/s |
| Thinner | MARINE THINNER |
| Thinning | 0–5% by volume |
The coating surface must be clean. Remove rust, dust, oil and other contaminants with high-pressure water, detergents or solvents.
| Preceding coat | ROSWAN QD HB, Alkyd Primer |
|---|---|
| Subsequent coat | - |
| Packaging | One-component |
Note: Resistance to specific cargo is limited; contact us.
2 Waiting time required before packing the first batch of goods
| Temperature | 10°C | 20°C | 30°C |
| Days | 50 | 40 | 30 |
3 Density, volume solids and volatile organic compound content are theoretical calculated values.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.