6437C MAXSTOP GS Epoxy High-build Anti-slip Paint is an epoxy coating. It has strong adhesion, good flexibility, impact and abrasion resistance, and high resistance to fresh water, salt water and oil. Parameters on this page: volume solids 70 ± 2%; dry film thickness 800 µm; theoretical spreading rate 1.14 L/m². Comparable products from the same brand: 5006 ALP 500 Epoxy Paint, 5055 BANNOH 500 Epoxy Paint, 5055D BANNOH 500 AC Epoxy Paint.
Source: CMP original technical data sheet (TDS) '6437C MAXSTOP GS Epoxy High-build Anti-slip Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 70 ± 2% |
|---|---|
| Dry Film Thickness | 800 µm |
| Theoretical Spreading Rate | 1.14 L/m2 |
| VOC | 285 g/L |
| Density / Specific Gravity | 1.90 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 82:18 (by volume) |
| Colour / Appearance | Green, grey |
MAXSTOP GS is a medium-roughness high-build epoxy anti-slip paint. Used for anti-slip surfacing in slippery areas.
It has high adhesion, good flexibility, impact resistance, abrasion resistance, and resistance to fresh water, salt water and oil.
Provides long periods without recoating, suitable for non-skid decks.
| Type | High-Build Epoxy Non-Skid |
|---|---|
| Use | For anti-slip decks and floors |
| Mixing Ratio | Base : curing agent = 82:18 (by volume) |
|---|---|
| Colour | Green, grey |
| Flash Point | Base 28.0 °C, curing agent 26.1 °C |
| Density | 1.90 g/ml |
| Volume Solids | 70 ± 2% |
| Volatile organic compound content | 285 g/L |
| Theoretical spreading rate | 1.14 L/m2 |
| Thickness | WFT 1143 µm |
| Dry film | 800 µm |
(dry film 200 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 5 h | 4 h | 2 h | 1.5 h |
| Hard Dry | 72 h | 50 h | 22 h | 15 h | |
| Recoat interval | At least | 72 h | 50 h | 22 h | 15 h |
| At most | - | - | |||
| Pot life | 7 h | 5 h | 4 h | 2 h | |
| Application method | Special spray equipment, brush, roller, trowel |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Thinner | EPOXY THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | BANNOH 500, BANNOH 1500 |
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with a mixer until homogeneous, then add the curing agent and mix with a power mixer. Then add the appropriate amount of thinner and mix.
3. Excessive thinner reduces sag resistance and film performance.
4. Excessive film thickness or insufficient air circulation will cause film defects (insufficient drying, insufficient strength and the like).
5. *Surface roughness is affected by the application method.
(*Consult the CMP sales department.) 6. Recommended dry film thickness of the previous compatible coat
| BANNOH 500 | 200 µm. 7. The minimum waiting time before first handling is as follows |
|---|
| Temperature: | 10°C | 20°C |
| Time: | 9 days | 5 days |
8. As an inherent property of epoxy coatings, chalking and fading under sunlight cannot be avoided.
9. VOC content and density are theoretical calculated values based on a representative colour formulation (green) without thinner. Values vary between colour formulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.