6196 UMEGUARD SUPER-H PRIMER QD Epoxy Paint is an epoxy paint, used as a primer. UMEGUARD SUPER-H PRIMER QD is an epoxy primer specially formulated in winter for UMEGUARD SUPER-H, with excellent physical properties such as roughness, abrasion resistance and adhesion, and excellent corrosion protection for dry cargo holds handling coal and iron. Parameters on this page: volume solids 63 ± 2%, dry film thickness 100–200 µm, theoretical spreading rate 0.16–0.32 L/m².
Data source: CMP original Technical Data Sheet (TDS), "6196 UMEGUARD SUPER-H PRIMER QD Epoxy Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 63 ± 2% |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.16-0.32 L/m2 |
| VOC | 394 g/L |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Grey, red-brown |
UMEGUARD SUPER-H PRIMER QD is an epoxy primer specially formulated in winter for UMEGUARD SUPER-H, with excellent physical properties such as roughness, abrasion resistance and adhesion, and excellent corrosion protection for dry cargo holds handling coal and iron.
It is suitable as a protective primer for cargo holds.
| Type | Epoxy |
|---|---|
| Use | May be used as an anticorrosive coating for the cargo holds of bulk carriers. |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Grey, red-brown |
| Flash Point | Base 23.1 °C, curing agent 24.9 °C |
| Volume Solids | 63 ± 2% |
| Volatile organic compound content | 394 g/L |
| Theoretical spreading rate | 0.16-0.32 L/m2 |
| Thickness | WFT 159–317 µm, DFT 100–200 µm |
(dry film 200 µm)
| Temperature | 5 °C | 10 °C | 20 °C | |
| Drying Time | Surface Dry | 5 h | 4.5 h | 3 h |
| Hard Dry | 17 h | 13 h | 8 h | |
| Recoat interval | At least | 17 h | 13 h | 8 h |
| At most | * | * | ||
| Pot life | 6 h | 5 h | ||
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.6-2.0 Pa.s |
| Nozzle | (Graco)621, 623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | CERABOND and others |
| Subsequent coat | UMEGUARD SUPER-H |
| Packaging | Two-component |
Note: 1. *Consult the CMP sales department.
2. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
3. Volume solids and VOC content are theoretical calculated values based on the formulation without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.