5106D EPICON PRIMER HB Epoxy Primer is an epoxy paint for use as a primer. It offers the following advantages: 1. Good durability keeps the film flexible for a long time. Parameters on this page: volume solids 57 ± 2% (ISO: 3233), dry film thickness 60–120 µm, theoretical spreading rate 0.105–0.211 L/m². Comparable products from the same brand: 1050 NZ PRIMER S zinc-free epoxy shop primer, 200 GALVANITE No.200 PRIMER epoxy galvanized steel primer, 400 GALVANITE No.400 PRIMER epoxy polyamide resin primer.
Parameter source: CMP manufacturer technical data sheet (TDS) '5106D EPICON PRIMER HB Epoxy Primer'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 60–120 µm |
| Theoretical Spreading Rate | 0.105-0.211 L/m2 |
| VOC | 427 g/L (Method 24) |
| Density / Specific Gravity | 1.33 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 70:30 (by volume) |
| Colour / Appearance | Light red-brown, brown |
EPICON PRIMER HB is a high-solids epoxy anti-corrosive primer. It offers the following advantages: 1. Good durability keeps the film flexible for a long time.
2. Good adhesion to previous and subsequent coats.
3. Good corrosion protection.
4. Good physical properties such as flexibility, impact resistance, abrasion resistance and adequate hardness.
5. Good oil and chemical resistance.
| Type | Epoxy primer |
|---|---|
| Use | Anti-corrosive primer for general steel structures. |
| Mixing Ratio | Base : curing agent = 70:30 (by volume) |
|---|---|
| Colour | Light red-brown, brown |
| Flash Point | Base 22°C; Hardener 27°C |
| Density | 1.33 g/ml (ISO: 2811) |
| Volume Solids | 57 ± 2% (ISO: 3233) |
| Volatile organic compound content | 427 g/L (Method 24) |
| Theoretical spreading rate | 0.105-0.211 L/m2 9.5-4.7 m2/L |
| Thickness | WFT 105–211 µm; 4.1–8.3 mils. DFT 60–120 µm; 2.4–4.7 mils |
( )
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3.5 h | 2 h | 1.5 h | 1 h |
| Hard Dry | 24 h | 18 h | 10 h | 8 h | |
| Recoat interval | At least | 24 h | 18 h | 10 h | 8 h |
| At most | 30 days | 30 days | |||
| Pot life | 24 h | 18 h | 12 h | 8 h | |
| Induction period | 30 min | - | |||
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 100 s (Ford Cup #4) |
| Nozzle | Graco719, 721 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–25% by volume |
If applied directly to steel surfaces, surface preparation shall reach ISO Sa 2 1/2; if applied over shop primer, surface preparation shall reach at least ISO St3.
| Preceding coat | EPICON ZINC HB-2, GALBON S-HB, CERABOND 2000 and other products |
|---|---|
| Subsequent coat | EPICON FINISH HB, EPICON UNDERCOAT EP,FLUOREX UNDERCOAT EX |
| Packaging | Two-component |
Density, solids content and volatile organic compound content are theoretical values calculated without thinner on the basis of a representative paint colour (light red-brown). Values vary with colour.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.