5530 EPICON A-100 PRIMER Epoxy Primer belongs to Epoxy and is used as a primer. EPICON A-100 PRIMER is composed mainly of epoxy resin, curing agent and pigments with good abrasion resistance on aluminium and aluminium alloys, and has good water resistance. Parameters on this page: Volume Solids 47 ± 2% (ISO: 3233), Dry Film Thickness 25–35 µm, Theoretical Spreading Rate 0.053–0.074 L/m². Comparable models from the same brand: 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Primer for Galvanized Steel, 400 GALVANITE No.400 PRIMER Epoxy Polyamide Resin Primer.
Parameter source: CMP original technical data sheet (TDS) “5530 EPICON A-100 PRIMER Epoxy Primer”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 47 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 25–35 µm |
| Theoretical Spreading Rate | 0.053-0.074 L/m2 |
| VOC | 496 g/L (Method 24) |
| Density / Specific Gravity | 1.08 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 71:29 (by volume) |
| Colour / Appearance | Off-white |
EPICON A-100 PRIMER is composed mainly of epoxy resin, curing agent and pigments with good abrasion resistance on aluminium and aluminium alloys, and has good water resistance.
| Type | Epoxy primer |
|---|---|
| Use | Primer for use on aluminium and aluminium alloys |
| Mixing Ratio | Base : curing agent = 71:29 (by volume) |
|---|---|
| Colour | Off-white |
| Flash Point | Base 23 °C Curing Agent 27.5 °C |
| Density | 1.08 g/mL (ISO: 2811) |
| Volume Solids | 47 ± 2% (ISO: 3233) |
| Volatile organic compound content | 496 g/L (Method 24) |
| Theoretical spreading rate | 0.053-0.074 L/m2 |
| Thickness | Wet film 53–74 µm Dry film 25–35 µm |
(dry film 35 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1 h | 45 min | 30 min | 20 min |
| Hard Dry | 12 h | 8 h | 6 h | 4 h | |
| Recoat interval | At least | 16 h | 12 h | 8 h | 6 h |
| At most | 7 days | 7 days | |||
| Pot life | 24 h | 20 h | 18 h | 12 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 20–50 s (Ford cup #4) |
| Nozzle | Graco413, 517 |
| Paint output pressure | 6.9-10.3 Mpa |
| Spray gun speed | 60–120 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–20% by volume |
Sanding required, then the surface shall be wiped with power washing, cleaner or solvent to remove rust, dust, grease and other contaminants
| Preceding coat | - |
|---|---|
| Subsequent coat | EPICON FINISH HB, EPICON MARINE HB-AL, BANNOH 200 and other products |
| Packaging | Two-component |
Density, volume solids and VOC content are theoretical values calculated without thinner. The values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.