6193A UMEGUARD SX HS Epoxy is an epoxy coating. It provides excellent physical properties such as strong adhesion, a tough film and good abrasion resistance. Parameters on this page: volume solids 77 ± 2% (ISO:3233), dry film thickness 100–200 µm, theoretical spreading rate 0.13–0.26 L/m². Comparable products of the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "6193A UMEGUARD SX HS Epoxy"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 77 ± 2% (ISO:3233) |
|---|---|
| Dry Film Thickness | 100–200 µm |
| Theoretical Spreading Rate | 0.13-0.26 L/m2 |
| VOC | 232 g/L (Method24) |
| Density / Specific Gravity | 1.47 g/mL (ISO:2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
| Colour / Appearance | Black, grey, green, red-brown, and similar |
UMEGUARD SX HS is a modified epoxy coating requiring minimal surface preparation. It provides excellent physical properties such as strong adhesion, a tough film and good abrasion resistance. It also provides excellent seawater corrosion resistance and cathodic protection performance.
| Type | Epoxy |
|---|---|
| Use | Suitable as an anticorrosive coating for ship bottoms, cargo holds, interior and exterior of accommodation spaces, void spaces, cofferdams, engine rooms, piping and other steel structures. Suitable for maintenance and repair. |
| Mixing Ratio | Base : curing agent = 81:19 (by volume) |
|---|---|
| Colour | Black, grey, green, red-brown, and similar |
| Flash Point | Base 29.2 °C, curing agent 27.2 °C |
| Density | 1.47 g/mL (ISO:2811) |
| Volume Solids | 77 ± 2% (ISO:3233) |
| Volatile organic compound content | 232 g/L (Method24) |
| Theoretical spreading rate | 0.13-0.26 L/m2 |
| Thickness | WFT 130–260 µm, DFT 100–200 µm |
(dry film 150 µm)
| Temperature | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 7 h | 3.5 h | 1.5 h |
| Hard Dry | 28 h | 12 h | 6 h | |
| Recoat interval | At least | 28 h | 12 h | 6 h |
| At most | 7 days | 5 days | ||
| Pot life | 5 h | 3 h | 1.5 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 10 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5-2.0 Pa.s |
| Nozzle | (Graco)419-623 |
| Paint output pressure | 15-25 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | CERABOND 2000, NZ PRIMER, EPICON ZINC RICH PRIMER B-2 and other products |
| Subsequent coat | EPICON FINISH HB, UNY MARINE and other products |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with a mixer until homogeneous, then add the curing agent and mix with a power mixer. Then add the appropriate amount of thinner and mix.
3. Excessive solvent may reduce sag resistance and film performance.
4. As an inherent property of modified epoxy coatings, UMEGUARD SX HS chalks and fades under UV light.
5. Waiting time before loading the first cargo
| Film thickness/temperature | 10°C | 20°C | 30°C |
| 200 µm (days) | 20 | 12 | 7 |
| 350 µm (days) | 30 | 18 | 11 |
6 VOC content, volume solids and density are theoretical values calculated without thinner. These values vary with colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.
The in-house item numbers of 6193A UMEGUARD SX HS Epoxy are as follows.Item No.is the most accurate form when ordering;Colour/colour codecorresponds to the actual colour (RAL, GSB are colour chart codes);Packaging SpecificationsFactory complete-set specification format. Colors not listed may be ordered against the colour card.
| Item No. | Colour / colour code | Packaging Specifications |
|---|---|---|
| 6193A UMEGUARD SX HS N8.0 | — | 14.8 L + 5.2 L |
| 6193A UMEGUARD SX HS QD RED BROWN | — | 20 L |
| 6193A UMEGUARD SX HS(MIO) | — | 20 L |
This model has a total of3item numbers, all listed on this page; colours outside the table (including special colours and bulk packaging) can be confirmed by phone, delivery dates are advised according to the factory's current production schedule and stock. In the packaging specification, the "+" indicates the complete-set notation for two-component products (base + curing agent), subject to the factory specification; a "—" in the colour column denotes an auxiliary product, or that the item has no colour code in the factory system.