6135W UMEGUARD SX QD Epoxy Coating is an epoxy coating. It provides physical properties such as strong adhesion, tough film, and good abrasion resistance, and resistance to pure water, seawater, and crude oil. Parameters on this page: volume solids 57 ± 2%, dry film thickness 100–250 µm, theoretical spreading rate 0.176–0.439 L/m². Comparable products of the same brand and type: 5006 ALP 500 Epoxy Coating, 5055 BANNOH 500 Epoxy Coating, 5055D BANNOH 500 AC Epoxy Coating.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "6135W UMEGUARD SX QD Epoxy Coating"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% |
|---|---|
| Dry Film Thickness | 100–250 µm |
| Theoretical Spreading Rate | 0.176-0.439 L/m2 |
| VOC | 435 |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
| Colour / Appearance | Black, grey, white, red-brown |
CHUGOKUMARINE PAINTS,LTD.
| Type | Epoxy |
|---|---|
| Use | It can be used as a protective coating for cargo holds, interior and exterior accommodation spaces, empty tanks, cofferdams, machinery spaces, piping, and other steel structures. |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
|---|---|
| Colour | Black, grey, white, red-brown |
| Flash Point | Base = 23.5°C, Hardener = 19°C |
| Volume Solids | 57±2% |
| Volatile organic compound content | :435 |
| Theoretical spreading rate | :0.176-0.439 L/m2 |
| Thickness | Wet film 176–439 µm; dry film 100–250 µm |
(dry film 250 µm)
| Temperature | -5°C | 0°C | 5°C | 10°C | 20°C | |
| Drying Time | Surface Dry | 8 h | 5 h | 2.5 h | 2 h | 1.5 h |
| Hard Dry | 40 h | 33 h | 20 h | 16 h | 14 h | |
| Recoat interval | At least | 40 h | 33 h | 20 h | 16 h | 14 h |
| At most | / | / | ||||
| Pot life | 20 h | 12 h | 6 h | |||
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | -5-20°C |
| Humidity | Maximum 85% RH |
| Apply by airless spray | Viscosity: 1.5–2.0 Pa·s |
| Nozzle | (Graco)623 |
| Paint output pressure | 14.7-17.7 Mpa. |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | WELBOND, CERABOND, NZ PRIMER, EPICON ZINC RICH PRIMER |
| Subsequent coat | EPICON MARINE FINISH HB, ACRI 700, and other products |
| Packaging | Two-component |
Note: 1. When applying in liquid tanks and confined areas, ventilation equipment must be installed to help solvent evaporation and promote drying and curing.
2. The ambient temperature during mixing of the base and hardener is most suitable above 10°C; otherwise additional thinner may be required to achieve the viscosity required for application.
3. Excess solvent may reduce sag resistance and film performance.
4. When the application temperature drops to -5°C or below, the curing reaction requires a longer time, and a higher temperature is required to achieve full cure.
| 5 | Curing time before first cargo loading |
|---|
| Temperature | 5°C | 10°C | 20°C |
| (days) | 25 | 16 | 10 |
| 6 | The volatile organic compound content is a theoretically calculated value. |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.