6135B BISCON HB-NT L QD Epoxy is an epoxy coating. In addition, it has excellent drying performance at low temperatures. Parameters on this page: volume solids 57 ± 2%, dry film thickness 100-250 µm, theoretical spreading rate 0.176-0.439 L/m². Comparable models from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) for 6135B BISCON HB-NT L QD Epoxy; spreading rate and other values are converted from TDS parameters and provided for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% |
|---|---|
| Dry Film Thickness | 100–250 µm |
| Theoretical Spreading Rate | 0.176-0.439 L/m2 |
| VOC | 435 |
| Density / Specific Gravity | — |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
| Colour / Appearance | Grey, black, white, red-brown |
HHUUK MARINE PAINTS, HT BISCON HB-NT L is a high-performance modified epoxy coating with strong adhesion, a tough and abrasion-resistant film and other excellent physical properties, and excellent chemical resistance to salt water, fresh water and crude oil.
In addition, it has excellent drying performance at low temperatures.
| Type | Epoxy |
|---|---|
| Use | May be used as a protective coating for cargo holds, the interior and exterior of accommodation areas, decks, topsides, void spaces, cofferdams, machinery spaces, pipelines and other steel structures. |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
|---|---|
| Colour | Grey, black, white, red-brown |
| Flash Point | Base 23.5 °C Curing agent 19.0 °C |
| Volume Solids | 57±2% |
| Volatile organic compound content | 435 |
| Theoretical spreading rate | 0.176-0.439 L/m2 |
| Thickness | Wet film 176-439 µm |
| Dry film | 100–250 µm |
(dry film 250 µm)
| Temperature | -5°C | 0°C | 5°C | 10°C | 20°C | |
| Drying Time | Surface Dry | 8 h | 5 h | 2.5 h | 2 h | 1.5 h |
| Hard Dry | 40 h | 33 h | 20 h | 16 h | 14 h | |
| Coating interval | At least | 40 h | 33 h | 20 h | 16 h | 14 h |
| At most* | * | * | * | |||
| Pot life | 20 h | 12 h | 6 h | |||
| Application method | Airless spray, brush, roller |
|---|---|
| Weather | Temperature: -5-20 °C; humidity: maximum 85% RH |
| Apply by airless spray | Viscosity: 1.5–2.0 Pa·s |
| Nozzle | Graco623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Preceding coat | WELBOND, CERBOND, NZ PRIMER, EPICON ZINC RICH PRIMER |
| Subsequent coat | EPICON FINISH HB, ACRI 700 FINISH J, etc. |
| Packaging | Two-component |
*Consult the CMP sales department. 1. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
2. The mixing temperature of the base and curing agent should be kept above 10 °C; otherwise, additional solvent must be added to reach the viscosity required for application.
3. Excessive solvent may cause sagging and reduced film performance.
4. Application is possible down to -5 °C, but hard dry takes a long time, and full cure is achieved only as the temperature rises.
| 5 | Waiting time before loading the first cargo |
|---|
| Temperature | 10°C | 20°C | 30°C |
| (days) | 25 | 16 | 10 |
6. The volatile organic compound content and density are theoretical values calculated for a representative colour formulation (grey) without thinner. The values differ for formulations of different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.