6135A BISCON HB-NT L Epoxy Coating belongs to epoxy coatings. CHUGOKUMARINE PAINTS,LTBISCON HB-NT L. is a high-performance modified epoxy coating with strong adhesion, a tough and abrasion-resistant film and other excellent physical properties, plus good chemical resistance to salt water, fresh water and crude oil. Parameters on this page: volume solids 57 ± 2%, dry film thickness 100–250 µm, theoretical spreading rate 0.175–0.439 L/m². Comparable products of the same brand: 5006 ALP 500 Epoxy Coating, 5055 BANNOH 500 Epoxy Coating, 5055D BANNOH 500 AC Epoxy Coating.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "6135A BISCON HB-NT L Epoxy Coating"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 57 ± 2% |
|---|---|
| Dry Film Thickness | 100–250 µm |
| Theoretical Spreading Rate | 0.175-0.439 L/m2 |
| VOC | 439 |
| Density / Specific Gravity | 1.36 |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
| Colour / Appearance | Grey, black, white, red-brown, green |
CHUGOKUMARINE PAINTS,LTBISCON HB-NT L. is a high-performance modified epoxy coating with excellent physical properties such as strong adhesion and a tough, abrasion-resistant film, and good chemical resistance to salt water, fresh water and crude oil.
| Type | Epoxy |
|---|---|
| Use | May be used as a protective coating for cargo holds, the interior and exterior of accommodation areas, decks, topsides, void spaces, cofferdams, machinery spaces, pipelines and other steel structures. |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
|---|---|
| Colour | Grey, black, white, red-brown, green |
| Flash Point | Base 23.5°C, Hardener 19.0°C |
| Density | 1.36 |
| Volume Solids | 57±2% |
| Volatile organic compound content | :439 |
| Theoretical spreading rate | 0.175-0.439 L/m2 |
| Thickness | Wet film 175–439 µm |
| Dry film | 100–250 µm |
(dry film 250 µm)
| Temperature | 5°C | 10°C | 20°C | 30°C | |
| Drying Time | Surface Dry | 4.5 h | 3.5 h | 2.5 h | 1.5 h |
| Hard Dry | 44 h | 27 h | 17 h | 12 h | |
| Recoat interval | At least | 44 h | 27 h | 17 h | 12 h |
| At most* | * | * | |||
| Pot life | 24 h | 14 h | 8 h | 5 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather | Temperature: minimum 5°C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Apply by airless spray | Viscosity: 1.5–2.0 Pa·s |
| Nozzle | Graco623 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | WELBOND, CERBOND, NZ PRIMER, EPICON ZINC RICH PRIMER |
| Subsequent coat | EPICON FINISH HB, ACRI 700 FINISH J, etc. |
| Packaging | Two-component |
*Consult the CMP sales department. 1. In confined spaces or at low temperatures, ventilation is necessary to remove the volatilised solvent and promote film formation during application and film formation.
| 2 | Waiting time before loading the first cargo |
|---|
| Temperature | 10°C | 20°C | 30°C |
| (days) | 20 | 12 | 7 |
3 Under natural conditions, chalking and fading in sunlight are unavoidable for BISCON HB-NT L as an epoxy coating.
4 The VOC content is a theoretical calculated value.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.