6075 CLEANKEEP 5000 HOLDING PRIMER Epoxy Primer is an epoxy paint, used as a primer. CLEANKEEP 5000 HOLDING PRIMER is mainly composed of epoxy resin and hardener, with excellent physical properties such as adhesion, roughness, abrasion resistance and pure water resistance. Parameters on this page: volume solids 34 ± 1%, dry film thickness 50 µm, theoretical spreading rate 0.147 L/m². Comparable products of the same brand: 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Galvanized Steel Primer, 400 GALVANITE No.400 PRIMER Epoxy Polyamide Resin Primer.
Data source: CMP original Technical Data Sheet (TDS), "6075 CLEANKEEP 5000 HOLDING PRIMER Epoxy Primer"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 34 ± 1% |
|---|---|
| Dry Film Thickness | 50 µm |
| Theoretical Spreading Rate | 0.147 L/m2 |
| VOC | 551 g/L |
| Density / Specific Gravity | 1.20 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 73:27 (by volume) |
| Colour / Appearance | Pink |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
CLEANKEEP 5000 HOLDING PRIMER is mainly composed of epoxy resin and hardener, with excellent physical properties such as adhesion, roughness, abrasion resistance and pure water resistance. It is specially used with CLEANKEEP 5000 and is useful as a protective primer for the interior of potable water tanks.
| Type | Epoxy primer |
|---|---|
| Use | Can be used as a temporary primer inside potable water tanks. |
| Mixing Ratio | Base : curing agent = 73:27 (by volume) |
|---|---|
| Colour | Pink |
| Flash Point | Base = 10.5 °C; hardener = 10.0 °C |
| Density | 1.20 g/ml |
| Volume Solids | 34 ± 1% |
| Volatile organic compound content | 551 g/L |
| Theoretical spreading rate | 0.147 L/m2 |
| Thickness | Wet film 147 µm; dry film 50 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3 h | 90 min | 40 min | 20 min |
| Hard Dry | 18 h | 8 h | 4 h | 2 h | |
| Recoat interval | At least | 18 h | 8 h | 4 h | 2 h |
| At most | 15 days | 15 days | |||
| Pot life | 24 h | 12 h | 8 h | 6 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 0.9-1.0PaS |
| Nozzle | (Graco)719 |
| Paint output pressure | 8.8-11.8 Mpa |
| Spray gun speed | 60–160 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–7% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2½ (ISO 8507-1 | 2007) or with power tools |
| power tools to St 3 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Optimum results can be achieved even on lightly corroded or damp steel surfaces.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2, NZ PRIMER S, etc. |
|---|---|
| Subsequent coat | CLEANKEEP 5000 |
| Packaging | Two-component |
Note: 1. Stir the base with a stirrer until uniform, then add the curing agent and mix with the base using a powerful stirrer. Then add an appropriate amount of thinner and mix.
2 Pot life is short. Mix only the required amount.
3 Volume solids, VOC content and density are theoretical calculated values based on the formulation without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.