6037 EPICON T-800 High-build Epoxy Phenolic Tank Coating is an epoxy coating. A protective coating for tank interiors, suitable for COT PSPC. Parameters on this page: volume solids 65 ± 2% [by volume] (ISO 3233); dry film thickness 75–160 µm; theoretical spreading rate 0.115–0.246 L/m². Comparable products from the same brand: 6033 EPICON T-800 HS High-build Epoxy Phenolic Tank Coating, 6037B EPICON T-800 QD High-build Epoxy Phenolic Tank Coating, 6035 EPICON T-800 HOLDING PRIMER Epoxy Phenolic Resin Temporary Anticorrosive Paint.
Source: CMP original technical data sheet (TDS) '6037 EPICON T-800 High-build Epoxy Phenolic Tank Coating'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 65 ± 2% [by volume] (ISO 3233) |
|---|---|
| Dry Film Thickness | 75–160 µm |
| Theoretical Spreading Rate | 0.115-0.246 L/m2 |
| VOC | 359 g/L (Method 24) |
| Density / Specific Gravity | 1.36 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER B |
| Mixing Ratio | Base : curing agent = 84:16 (by volume) |
| Colour / Appearance | Grey, light grey, red-brown |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EPICON T-800 is a high-build epoxy phenolic coating with strong adhesion, tough film, abrasion resistance and other high physical properties, plus high chemical resistance to saltwater, fresh water, petroleum products, crude oil, alkalis and weak acids. A protective coating for tank interiors, suitable for COT PSPC. One airless spray coat can reach a dry film thickness of 75–160 µm.
| Type | High-Build Epoxy Phenolic Tank Coating |
|---|---|
| Use | Suitable as a topcoat for oil tanks, chemical tanks and the like |
| Mixing Ratio | Base : curing agent = 84:16 (by volume) |
|---|---|
| Colour | Grey, light grey, red-brown |
| Flash Point | Base 17.5 °C, curing agent 7.5 °C |
| Density | 1.36 g/ml (ISO: 2811) |
| Volume Solids | 65 ± 2% [by volume] (ISO 3233) |
| Volatile organic compound content | 359 g/L (Method 24) |
| Theoretical spreading rate | 0.115-0.246 L/m2 |
| Thickness | WFT 115–246 µm, DFT 75–160 µm |
(dry film 125 µm)
| Temperature | 10 °C | 20 °C | 30 °C | 40 °C | |
| Drying Time | Surface Dry | 2.5 h | 1.5 h | 30 min | 15 min |
| Hard Dry | 24 h | 12 h | 6 h | 4 h | |
| Recoat interval | At least | 24 h | 16 h | 14 h | 8 h |
| At most* | 28 days | 21 days | 14 days | 10 days | |
| At most** | 10 days | 7 days | 5 days | 3 days | |
| Pot life | 7 h | 5 h | 3 h | 1.5 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 10 °C |
| Humidity | Maximum 85% RH; steel temperature at least 5 °C above the dew point |
| Airless spray: viscosity | 1.0-1.8Pa.S |
| Nozzle | Graco619, 621, 623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER B |
| Thinning | 0–10% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2½ (ISO 8507-1 | 2007) or with power |
| power tools to St 3 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Optimum results can be achieved even on lightly corroded or damp steel surfaces.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | EPICON T-800 HOLDING PRIMER, EPICON T-800, EPICON T-800 QD, CERABOND 2000 |
|---|---|
| Subsequent coat | EPICON T-800 |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with an electric stirrer to a uniform state, then thoroughly stir all of the curing agent with the base. Finally add an appropriate amount of thinner and mix thoroughly.
3. Excessive solvent may reduce sag resistance. 4. Mix only the amount of paint that can be used within the specified pot life.
5. *(1) Shade netting is recommended over the coating surface to avoid direct sunlight through manholes or other openings.
If the coating surface has been directly exposed to sunlight, the above “**” indicates the maximum recoat interval
| 6. on steel | Dew point + minimum 5 °C |
|---|---|
| on the film | Dew point + minimum 3 °C. 7. Volume solids, VOC content and density are theoretically calculated from a representative formulation without thinner. Values vary with colour formulation. |
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.