6032 EPICON T-500 HS High-build Epoxy Tank Lining Coating is an epoxy paint. Using airless spray, one coat can achieve a dry film thickness of 100–160 µm. Parameters on this page: volume solids 74 ± 2%, dry film thickness 100–160 µm, theoretical spreading rate 0.135–0.216 L/m². Comparable products of the same brand: 5006 ALP 500 Epoxy Paint, 5055 BANNOH 500 Epoxy Paint, 5055D BANNOH 500 AC Epoxy Paint.
Data source: CMP original Technical Data Sheet (TDS), "6032 EPICON T-500 HS High-build Epoxy Tank Lining Coating"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 74 ± 2% |
|---|---|
| Dry Film Thickness | 100–160 µm |
| Theoretical Spreading Rate | 0.135-0.216 L/m2 |
| VOC | 267 g/L |
| Density / Specific Gravity | 1.48 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER B |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
| Colour / Appearance | Red-brown, grey, light grey |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EPICON T-500 HS is a high-build epoxy coating with excellent physical properties such as strong adhesion, tough film and abrasion resistance, and excellent chemical resistance to salt water, fresh water, petroleum products, crude oil, alkaline substances and weak acids. Suitable as a protective coating for tank interiors. Suitable for COT PSPC. Using airless spray, one coat can achieve a dry film thickness of 100–160 µm.
| Type | High-Build Epoxy Tank Coating |
|---|---|
| Use | Suitable as a topcoat for oil tanks, fresh water tanks, cargo holds, solvent tanks, chemical tanks and the like |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
|---|---|
| Colour | Red-brown, grey, light grey |
| Flash Point | Base 17.5 °C; hardener 46.5 °C |
| Density | 1.48 g/ml |
| Volume Solids | 74 ± 2% |
| Volatile organic compound content | 267 g/L |
| Theoretical spreading rate | 0.135-0.216 L/m2 |
| Thickness | Wet film 135–216 µm; dry film 100–160 µm |
(dry film 125 µm)
| Temperature | 10 °C | 20 °C | 30 °C | 40 °C | |
| Drying Time | Surface Dry | 2.5 h | 1.5 h | 30 min | 15 min |
| Hard Dry | 24 h | 12 h | 6 h | 4 h | |
| Recoat interval | At least | 24 h | 16 h | 14 h | 8 h |
| At most* | 28 days | 21 days | 14 days | 10 days | |
| At most** | 10 days | 7 days | 5 days | 3 days | |
| Pot life | 6 h | 4 h | 2.5 h | 1 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 10 °C; steel temperature at least 5 °C above the dew point*** |
| Airless spray: viscosity | 1.3-1.8Pa.S |
| Nozzle | Graco619,621,623 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER B |
| Thinning | 0–10% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2½ (ISO 8507-1 | 2007) or by |
| power tool to St3 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Optimum results can be achieved even on lightly corroded or damp steel surfaces.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | CERABOND2000 |
|---|---|
| Subsequent coat | EPICON T-500 HS |
| Packaging | Two-component |
Note: 1. In confined spaces or restricted spaces at low temperature, ventilation is necessary to remove volatilised solvent and promote film formation during application and drying.
2. Stir the base with an electric stirrer to a uniform state, then thoroughly stir all of the curing agent with the base. Finally add an appropriate amount of thinner and mix thoroughly.
3. Excessive solvent may reduce sag resistance. 4. Mix only the amount of paint that can be used within the specified pot life.
5. *(1) Shade netting is recommended over the coating surface to avoid direct sunlight through manholes or other openings.
Inside.
6 **Indicates outdoor exposure
| 7. ***on steel | Dew point + minimum 5 °C |
|---|---|
| on the film | Dew point + minimum 3 °C. 8 Density, volume solids and VOC content are theoretical calculated values based on a representative formulation (red brown) without thinner. The values vary with different colour formulations. |
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.