5988 CMP BIOCLEAN SG Polyurethane is a polyurethane coating. MARINE PAINTS, LTD. CMP BIOCLEAN SG is a three-component anticorrosive coating used in the CMP BIOCLEAN system. Parameters on this page: volume solids 61 ± 2% (ISO: 3233), dry film thickness 100 µm, theoretical spreading rate 0.164 L/m². Comparable products from the same brand: 5988C CMP BIOCLEAN SG QD Polyurethane, 5988D CMP BIOCLEAN SG UQD Polyurethane, 5510B THERMO SHADAN PU Polyurethane Topcoat.
Source: CMP original technical data sheet (TDS) "5988 CMP BIOCLEAN SG Polyurethane"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 61 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 100 µm |
| Theoretical Spreading Rate | 0.164 L/m2 |
| VOC | 394 gq/L (Method 24) |
| Density / Specific Gravity | 1.31 ge/ml (ISO:2811) |
| Number of Components | Three-component |
| Thinner | URETHANE THINNER B |
| Mixing Ratio | Base : curing agent : additive = 71.6:23.8:4.6 (by volume) |
| Colour / Appearance | Grey |
HUGOKUMARINE PAINTS,LTD.
| Type | Polyurethane, fluorocarbon |
|---|---|
| Use | Can be used as the primer of the CMP BIOCLEAN antifouling system. |
| Mixing Ratio | Base : curing agent : additive = 71.6:23.8:4.6 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | Base 16 °C Curing agent 1 °C Additive 23 °C |
| Density | 1.31 ge/ml (ISO:2811) |
| Volume Solids | 61±2% (ISO: 3233) |
| Volatile organic compound content | 394 gq/L (Method 24) |
| Theoretical spreading rate | 0.164 L/m2 |
| Thickness | WFT 164 µm |
| Dry film | 100 µm |
(dry film = 100 µm)
| Temperature | 15°C | 20°C | 30°C | |
| Drying Time | Surface Dry | 1.5 h | 1 h | 30 min |
| Hard Dry | 3 h | 2 h | 1 h | |
| Recoat interval | All — minimum | 5 h | 3 h | 2 h |
| At most* | - |
|---|---|
| Pot life | 45 minutes 45 minutes 30 minutes |
| Application method | Airless spray, brush |
|---|---|
| Weather | Temperature: minimum 15 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.6-2.0 Pa.S |
| Nozzle | Graco517-723 |
| Paint output pressure | 15-20 Mpa |
| Spray gun speed | 60-80 cm/s |
| Thinner | URETHANE THINNER B |
| Thinning | 0–7% by volume |
| Preceding coat | BANNOH 500 |
| Subsequent coat | CMP BIOCLEAN HB, CMP BIOCLEAN R |
| Packaging | Three-component |
2 Density, volume solids and volatile organic content are theoretical values calculated from the formulation without thinner.
Values differ for different colour formulations or different test standards.
The text on this page was generated by OCR of the manufacturer's TDS; individual characters may differ from the original. The manufacturer's TDS prevails.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.