5542 EPICON B-100 PRIMER Epoxy Primer is an epoxy coating for use as a primer. EPICON B-100 PRIMER is a two-component epoxy primer for brass surfaces, mainly composed of epoxy resin, curing agent and pigments. Parameters on this page: volume solids 50 ± 2% (ISO: 3233), dry film thickness 70 µm, theoretical spreading rate 0.14 L/m². Similar models from the same brand for comparison: 1050 NZ PRIMER S zinc-free epoxy shop primer, 200 GALVANITE No.200 PRIMER epoxy galvanized steel primer, 400 GALVANITE No.400 PRIMER epoxy polyamide resin primer.
Parameter source: CMP original technical data sheet (TDS) 5542 EPICON B-100 PRIMER Epoxy Primer; values such as spreading rate are converted from TDS parameters for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 50 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 70 µm |
| Theoretical Spreading Rate | 0.14 L/m2 |
| VOC | 470 g/L (Method 24) |
| Density / Specific Gravity | 1.33 g/ml (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
| Colour / Appearance | Yellow |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EPICON B-100 PRIMER is a two-component epoxy primer for brass surfaces, mainly composed of epoxy resin, curing agent and pigments.
It has good adhesion and water resistance on brass surfaces.
| Type | Epoxy primer |
|---|---|
| Use | Can be used for copper propellers of ocean-going vessels. |
| Mixing Ratio | Base : curing agent = 78:22 (by volume) |
|---|---|
| Colour | Yellow |
| Flash Point | Base 26.0°C, curing agent 20.0°C |
| Density | 1.33 g/ml (ISO: 2811) |
| Volume Solids | 50 ± 2% (ISO: 3233) |
| Volatile organic compound content | 470 g/L (Method 24) |
| Theoretical spreading rate | 0.14 L/m2 |
| Thickness | WFT 140 µm, DFT 70 µm |
( )
| Temperature | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 2 h | 1.5 h | 60 min | 30 min | 20 min |
| Hard Dry | 12 h | 8 h | 6 h | 3 h | 2 h | |
| Recoat interval | At least | 12 h | 8 h | 6 h | 3 h | 2 h |
| At most | 7 days | 7 days | 5 days | 3 days | ||
| Pot life | 70 min | 60 min | 45 min | 30 min | ||
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 90–100 s (Ford Cup #4) |
| Nozzle | Graco519 - 621 |
| Paint output pressure | 6.9-10.3 Mpa |
| Spray gun speed | 60–120 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–5% by volume |
| Requirement | Copper slag abrasive blasting |
|---|---|
| Preceding coat | - |
| Subsequent coat | CMP BIOCLEAN SG-R |
| Packaging | Two-component |
Note: 1 Due to the short pot life, use immediately after mixing.
2. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
3. Stir the base with a power mixer until homogeneous, then stir all of the curing agent and base thoroughly. Finally, add the appropriate amount of thinner and mix thoroughly.
4 Density, volume solids and VOC content are theoretical calculated values without thinner addition.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.