5540 EPICON S-100 PRIMER Epoxy Primer belongs to Epoxy and is used as a primer. EPICON S-100 PRIMER is a two-component primer for stainless steel, mainly composed of epoxy resin, curing agent and pigments. Parameters on this page: Volume Solids 29 ± 2%, Dry Film Thickness (DFT) 25–35 µm, Theoretical Spreading Rate 0.086–0.121 L/m². Comparable models from the same brand: 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Primer for Galvanized Steel, 400 GALVANITE No.400 PRIMER Epoxy Polyamide Resin Primer.
Parameter source: CMP original Technical Data Sheet (TDS) “5540 EPICON S-100 PRIMER Epoxy Primer”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 29 ± 2% |
|---|---|
| Dry Film Thickness | 25–35 µm |
| Theoretical Spreading Rate | 0.086-0.121 L/m2 |
| VOC | 598 g/L |
| Density / Specific Gravity | 1.17 g/ml |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER G |
| Mixing Ratio | Base : curing agent = 87:13 (by volume) |
| Colour / Appearance | Brown-red |
EPICON S-100 PRIMER is a two-component primer for stainless steel, mainly composed of epoxy resin, curing agent and pigments.
It exhibits good adhesion and water resistance on stainless steel.
| Type | Epoxy primer |
|---|---|
| Use | Can be used as a primer on aluminium and stainless steel |
| Mixing Ratio | Base : curing agent = 87:13 (by volume) |
|---|---|
| Colour | Brown-red |
| Flash Point | Base 16.5 °C Curing Agent 19.5 °C |
| Density | 1.17 g/ml |
| Volume Solids | 29 ± 2% |
| Volatile organic compound content | 598 g/L |
| Theoretical spreading rate | 0.086-0.121 L/m2 |
| Thickness | Wet Film Thickness (WFT) 86–121 µm Dry Film Thickness (DFT) 25–35 µm |
( )
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 10 min | 8 min | 5 min | 4 min |
| Hard Dry | 12 h | 9 h | 6 h | 4 h | |
| Recoat interval | At least | 16 h | 12 h | 8 h | 6 h |
| At most | 7 days | 7 days | |||
| Pot life | 36 h | 30 h | 24 h | 16 h | |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 20–24 s (Ford Cup #4) |
| Nozzle | Graco413, 517 |
| Paint output pressure | 6.9-10.3 Mpa |
| Spray gun speed | 60–120 cm/s |
| Thinner | EPOXY THINNER G |
| Thinning | 0–20% by volume |
Remove oil, grease, dust, salt and other contaminants with high-pressure water, detergent or solvent.
The surface must be thoroughly dry.
| Preceding coat | - |
|---|---|
| Subsequent coat | Various coatings (except inorganic coatings and polyurethane coatings*) |
| Packaging | Two-component |
Note: 1. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
2 Stir with a mixer until uniform, then add the appropriate thinner and mix.
3 Adding excessive thinner will reduce sag resistance and film performance.
4* When applying polyurethane coatings, BANNOH 500 is required as primer.
5 Density, volume solids and volatile organic compound content are theoretical values without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.