5402D EPICON FINISH HB EX Epoxy Topcoat belongs to epoxy coatings and is used as a topcoat. EPICON FINISH HB EX is a high-build topcoat based on epoxy polyamide resin. Parameters on this page: volume solids 51 ± 2% (ISO: 3233), dry film thickness 30–100 µm, theoretical spreading rate 0.059–0.196 L/m². Comparable models from the same brand: 5402C EPICON FINISH HB Epoxy Topcoat, 5412A EPICON FINISH HS Epoxy Topcoat, 100 EVASIGN No.100 Modified Alkyd Topcoat.
Parameter source: CMP original technical data sheet (TDS) for 5402D EPICON FINISH HB EX Epoxy Topcoat; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 51 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 30–100 µm |
| Theoretical Spreading Rate | 0.059-0.196 L/m2 |
| VOC | 468 g/L (Method 24) |
| Density / Specific Gravity | 1.27 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
| Colour / Appearance | White |
EPICON FINISH HB EX is a high-build topcoat based on epoxy polyamide resin. It provides excellent durability and adhesion. It can be used as a topcoat for steel ships, bridges and steel structures.
| Type | Epoxy topcoat |
|---|---|
| Use | Suitable as an exterior topcoat of the epoxy series for factories, bridges, oil storage tank exteriors and other steel structures. |
| Mixing Ratio | Base : curing agent = 67:33 (by volume) |
|---|---|
| Colour | White |
| Flash Point | Base 24°C Curing agent 27.5°C |
| Density | 1.27 g/mL (ISO: 2811) |
| Volume Solids | 51 ± 2% (ISO: 3233) |
| Volatile organic compound content | 468 g/L (Method 24) |
| Theoretical spreading rate | 0.059-0.196 L/m2 |
| Thickness | WFT 59–196 µm |
| Dry film | 30–100 µm |
(dry film 100 µm)
| Temperature | -5 °C | 10 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 5.5 h | 4.5 h | 3.5 h | 2.5 h | 1.5 h | 1 h |
| Hard Dry | 55 h | 38 h | 28 h | 16 h | 12 h | ||
| Recoat interval | At least | 55 h | 44 h | 24 h | 18 h | 10 h | 8 h |
At most*
| Pot life | 24 h, 24 h, 24 h, 24 h, 18 h, 12 h |
|---|
| Application method | Airless Spray |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.5Pa.s |
| Nozzle | Graco719, 721 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–7% by volume |
Surfaces shall be clean; remove rust, dust, grease and other contaminants by power washing, detergent or solvent wiping.
| Preceding coat | Such as EPICON PRIMER HB, EPICON UNDERCOAT |
|---|---|
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1 * Refer to the application specification. 2 In confined spaces or limited spaces under low-temperature conditions, ventilation equipment is necessary to remove evaporated solvent during application and film formation and to promote paint film formation.
3. Stir the base with a power mixer until homogeneous, then stir all of the curing agent and base thoroughly. Finally, add the appropriate amount of thinner and mix thoroughly.
4 Excess solvent may reduce sag resistance.
5 Application at -5°C is possible, but a long time is required to reach hard dry, and full cure is achieved only as the temperature rises.
6 Due to the characteristics of epoxy coatings, EPICON FINISH HB cannot avoid chalking and fading under UV exposure.
7. Density, volume solids and VOC content are theoretical calculated values without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.