5085 BANNOH 1500 QD Epoxy belongs to epoxy coatings. It provides good adhesion, a tough film, abrasion resistance and many other physical properties, as well as excellent flexibility, seawater corrosion resistance and cathodic protection resistance. Parameters on this page: volume solids 73 ± 2% (ISO: 3233), dry film thickness 75–250 µm, theoretical spreading rate 0.103–0.342 L/m2. Comparable products of the same brand and type: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) \"5085 BANNOH 1500 QD Epoxy\"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 73 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 75–250 µm |
| Theoretical Spreading Rate | 0.103-0.342 L/m2 |
| VOC | 286 g/L (Method 24) |
| Density / Specific Gravity | 1.40 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
| Colour / Appearance | Grey, light grey, red-brown, cream yellow, white, black |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
BANNOH 1500 QD is a multi-purpose primer. It has good adhesion, a tough film, abrasion resistance and many other physical properties, and provides excellent flexibility, seawater corrosion resistance and cathodic protection resistance.
This product is an IMO PSPC-certified coating for WBT and COT and is suitable for many areas of the hull. It can also be applied under cold climate conditions.
| Type | Epoxy |
|---|---|
| Use | For anti-corrosion of hull shell, superstructures, external decks and ballast tanks |
| Mixing Ratio | Base : curing agent = 79:21 (by volume) |
|---|---|
| Colour | Grey, light grey, red-brown, cream yellow, white, black |
| Flash Point | Base 28 °C, curing agent 27.4 °C |
| Density | 1.40 g/mL (ISO: 2811) |
| Volume Solids | 73 ± 2% (ISO: 3233) |
| Volatile organic compound content | 286 g/L (Method 24) |
| Theoretical spreading rate | 0.103-0.342 L/m2 |
| Thickness | WFT 103–342 µm |
| Dry film | 75–250 µm |
(dry film 200 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 15 h | 10 h | 9 h | 7 h | 3 h | 1.5 h |
| Hard Dry | 36 h | 24 h | 20 h | 14 h | 8 h | 3.5 h | |
| Recoat interval | At least | 36 h | 24 h | 20 h | 14 h | 8 h | 3.5 h |
| At most* | * | * | * | ||||
| Pot life | 7 h | 5 h | 3.5 h | 2 h | 1 h | ||
| Application method | Airless spray, brush |
|---|---|
| Weather | Temperature: minimum -5 °C |
| Humidity | Maximum 85% RH |
| Apply by airless spray | Viscosity: 1.6–2.0 Pa·s |
| Nozzle | Graco519-723 |
| Paint output pressure | 15-25 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Newbuilding | Follow the shipyard standard or the IMO PSPC standard. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease, etc. Remove salts and other contaminants with high-pressure fresh water, then dry completely. Use abrasive |
| material to remove damaged areas to at least Sa2 (ISO 8507-1 | 2007) or use power tools to achieve St3 |
| (ISO 8507-1 | 2007). For areas required to comply with IMO PSPC, operate strictly in accordance with the regulation. |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2, among others |
|---|---|
| Subsequent coat | BANNOH 500 N, BANNOH 1500 N, EPICON FINISH HB, etc. |
| Packaging | Two-component |
Note: 1. Consult the CMP sales department.
2. To remove volatilised solvent and promote film formation during application and drying, ventilation is necessary.
3. Stir the base with a power mixer until homogeneous, then stir all of the curing agent and base thoroughly. Finally, add the appropriate amount of thinner and mix thoroughly.
4. Excessive thinner reduces the sag resistance and physical properties of the paint film.
5 Application can be carried out at temperatures below -5 °C, but film formation will take longer, and complete film formation requires waiting until the temperature rises.
6. Waiting time before first cargo loading
| Film thickness/temperature | 5°C | 10°C | 20°C |
| 200 µm (days) | 25 | 16 | 9 |
| 350 µm (days) | 37 | 24 | 14 |
7 Density, solids content and volatile organic compound content are calculated without thinner. These values vary depending on colour, production process and local regulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.