5084K BANNOH 1500 S Z Epoxy belongs to Epoxy. 2. Excellent recoating performance with antifouling coatings. Parameters on this page: Volume Solids 64 ± 2% (ISO: 3233), Theoretical Spreading Rate 0.156–0.391 L/m2, Number of Components two-component. Comparable models from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Parameter source: CMP original technical data sheet (TDS) "5084K BANNOH 1500 S Z Epoxy"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 64 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 100–250 µm |
| Theoretical Spreading Rate | 0.156-0.391 L/m2 |
| VOC | 333 g/L (Method 24) |
| Density / Specific Gravity | 1.41 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
| Colour / Appearance | Light grey, dark purple |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
| Type | Epoxy |
|---|---|
| Use | Used as an anti-corrosive tie coat for the hull shell |
| Mixing Ratio | Base : curing agent = 85:15 (by volume) |
|---|---|
| Colour | Light grey, dark purple |
| Flash Point | Base 25.7 °C, curing agent 27.7 °C |
| Density | 1.41 g/mL (ISO: 2811) |
| Volume Solids | 64 ± 2% (ISO: 3233) |
| Volatile organic compound content | 333 g/L (Method 24) |
| Theoretical spreading rate | 0.156 - 0.391 L/m2 |
| Thickness | WFT 156–391 µm |
| Dry film | 100–250 µm |
(dry film 200 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 6 h | 4 h | 3 h | 2 h |
| Hard Dry | 40 h | 24 h | 15 h | 10 h | |
| Recoat interval | At least | 24 h | 16 h | 10 h | 8 h |
| At most* | * | * | |||
| Pot life | 18 h | 12 h | 6 h | 3 h | |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 1.8-2.2Pa.s |
| Nozzle | Graco619, 621, 623 |
| Paint output pressure | 15-25 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2 (ISO 8507-1 | 2007) or with power tools |
| power tools to St 3 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | CERABOND 2000, EPICON ZINC RICH PRIMER B-2 |
|---|---|
| Subsequent coat | SEA GRANDPRIX series, SEAFLO NEO, SEAFLO NEO SL, SEAFLO NEO Z, SEAFLO NEO FLAT Z, UNYMARINE, EPICON FINISH HB, etc. |
| Packaging | Two-component |
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.