5083 BANNOH 2000 QD Epoxy is an epoxy coating. It has good adhesion, a tough film and abrasion resistance, among other physical properties, as well as excellent flexibility, resistance to seawater corrosion and cathodic protection. Parameters on this page: volume solids 80 ± 2%, dry film thickness 75–250 µm, theoretical spreading rate 0.094–0.312 L/m². Comparable products from the same brand: 5006 ALP 500 Epoxy, 5055 BANNOH 500 Epoxy, 5055D BANNOH 500 AC Epoxy.
Source: CMP original technical data sheet (TDS) "5083 BANNOH 2000 QD Epoxy"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 80 ± 2% |
|---|---|
| Dry Film Thickness | 75–250 µm |
| Theoretical Spreading Rate | 0.094-0.312 L/m2 |
| VOC | 189 g/L |
| Density / Specific Gravity | 1.50 g/mL |
| Number of Components | Two-component |
| Thinner | EPOXY THINNER A |
| Mixing Ratio | Base : curing agent = 75:25 (by volume) |
| Colour / Appearance | Red-brown, light grey |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
BANNOH 2000 QD is a multipurpose high-solids epoxy primer. It has good adhesion, a tough film and abrasion resistance, among other physical properties, as well as excellent flexibility, resistance to seawater corrosion and cathodic protection.
This product is a WBT and COT coating certified to IMO PSPC and is suitable for many areas of the hull.
| Type | Epoxy |
|---|---|
| Use | For anti-corrosion of hull shell, superstructures, external decks and ballast tanks |
| Mixing Ratio | Base : curing agent = 75:25 (by volume) |
|---|---|
| Colour | Red-brown, light grey |
| Flash Point | Base 32.5 °C, curing agent 27 °C |
| Density | 1.50 g/mL |
| Volume Solids | 80 ± 2% |
| Volatile organic compound content | 189 g/L |
| Theoretical spreading rate | 0.094-0.312 L/m2 |
| Thickness | WFT 94–313 µm |
| Dry film | 75–250 µm |
(dry film 200 µm)
| Temperature | -5 °C | 0 °C | 5 °C | 10 °C | 20 °C | |
| Drying Time | Surface Dry | 12 h | 9 h | 7 h | 4 h | 1 h |
| Hard Dry | 36 h | 24 h | 17 h | 10 h | 5 h | |
| Recoat interval | At least | 36 h | 24 h | 17 h | 10 h | 5 h |
| At most* | * | * | ||||
| Pot life | 10 h | 8 h | 6 h | 4 h | 2 h | |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum -5 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 1.5-2.0Pa.s |
| Nozzle | Graco619, 621, 623 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | EPOXY THINNER A |
| Thinning | 0–15% by volume |
| Newbuilding | Follow the shipyard standard or the IMO PSPC standard. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil, grease and the like. Remove salts and other contaminants with high-pressure fresh water, then dry completely. Remove |
| damaged areas to at least Sa2 (ISO 8507-1 | 2007), or prepare to St3 with power tools (ISO 8507-1:2007). For areas subject to IMO PSPC requirements, operate strictly in accordance with the regulations. |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | CERABOND, EPICON ZINC RICH PRIMER B-2, etc. |
|---|---|
| Subsequent coat | BANNOH 500 N, UNYMARINE, EPICON MARINE HB, among others |
| Packaging | Two-component |
Note: 1. Consult the CMP sales department.
2. To remove volatilised solvent and promote film formation during application and drying, ventilation is necessary.
3. Stir the base with a power mixer until homogeneous, then stir all of the curing agent and base thoroughly. Finally, add the appropriate amount of thinner and mix thoroughly.
4. Excessive thinner reduces the sag resistance and physical properties of the paint film.
5. Usable at -5 °C, but curing takes longer; full cure is achieved only as the temperature rises.
6. If the coated surface is exposed to direct sunlight, the subsequent coat should be sprayed as soon as possible within the minimum spray interval.
7. Density and VOC content are calculated from a representative colour (light grey) of the paint without thinner. Values vary with colour.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.