4008 CMP AC Special Synthetic Resin Anti-rust Paint is a primer. CMP AC is a coating composed of a special synthetic resin, providing fast drying, recoating and good corrosion protection. Parameters on this page: volume solids 47 ± 2% (ISO: 3233), dry film thickness 40–75 µm, theoretical spreading rate 0.085–0.160 L/m². Comparable products of the same brand and category: 3007 SILVAX SQ-K Vinyl Resin Primer, 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Galvanized Steel Plate Primer.
Parameter source: CMP manufacturer's Technical Data Sheet (TDS) "4008 CMP AC Special Synthetic Resin Anti-rust Paint"; values including spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 47 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 40–75 µm |
| Theoretical Spreading Rate | 0.085-0.160 L/m2 |
| VOC | 486 g/L (Method 24) |
| Density / Specific Gravity | 1.30 g/mL (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 27.0°C |
| Thinner | CR/ACRI THINNER A |
| Colour / Appearance | Silver, silver-red |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
CMP AC is a coating composed of a special synthetic resin; it provides fast drying and overcoating and good corrosion protection. It has seawater resistance and good compatibility with subsequent coatings.
| Type | Special Synthetic Resin Anti-corrosive Paint |
|---|---|
| Use | Ship hull plating and other steel structures |
| Colour | Silver, silver-red |
|---|---|
| Flash Point | 27.0°C |
| Density | 1.30 g/mL (ISO: 2811) |
| Volume Solids | 47 ± 2% (ISO: 3233) |
| Volatile organic compound content | 486 g/L (Method 24) |
| Theoretical spreading rate | 0.085-0.160 L/m2 |
| Thickness | WFT 85–160 µm |
| Dry film | 40–75 µm |
( )
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1 h | 45 min | 30 min | 20 min |
| Hard Dry | 6 h | 4.5 h | 3 h | 2.5 h | |
| Recoat interval | At least | 12 h | 8 h | 6 h | 5 h |
At most
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 140 s (Ford Cup #4) |
| Nozzle | Graco721, 723 |
| Paint output pressure | 14.7-17.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | CR/ACRI THINNER A |
| Thinning | 0–7% by volume |
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
|---|---|
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2 (ISO 8507-1 | 2007) or with power tools |
| tool to St2 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | NZ PRIMER, EPICON ZINC RICH PRIMER, CERABOND and other products |
|---|---|
| Subsequent coat | ACRI 700 FINISH ST, SEATENDER series, SEA GRANDPRIX series and other products |
| Packaging | One-component |
Density and volatile organic compound content are calculated without thinner. Values may vary depending on colour, production process, and other factors.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.