3007 SILVAX SQ-K Vinyl Resin Primer is a primer. SILVAX SQ-K, a modified vinyl coating, forms a water-resistant sealer coat and provides an excellent foundation for subsequently applied antifouling coatings. Parameters on this page: Volume Solids 30 ± 2% (ISO: 3233), Dry Film Thickness (DFT) 40–80 µm, Theoretical Spreading Rate 0.133–0.267 L/m². Comparable models from the same brand: 4008 CMP AC Special Synthetic Resin Anti-corrosive Paint, 1050 NZ PRIMER S Zinc-free Epoxy Shop Primer, 200 GALVANITE No.200 PRIMER Epoxy Primer for Galvanized Steel.
Parameter source: CMP original technical data sheet (TDS) “3007 SILVAX SQ-K Vinyl Resin Primer”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 30 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 40–80 µm |
| Theoretical Spreading Rate | 0.133-0.267 L/m2 |
| VOC | 615 (Method 24) |
| Density / Specific Gravity | 1.08 g/L (ISO: 2811) |
| Number of Components | One-component |
| Flash Point | 18.8°C |
| Thinner | VINYL THINNER |
| Colour / Appearance | Silver, silver-pink |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
SILVAX SQ-K, modified vinyl coating, forms a water-resistant sealer coat and provides an excellent foundation for subsequently applied antifouling paint.
| Type | Vinyl Primer |
|---|---|
| Use | For ship bottom steel plates, used as a tie coat for antifouling paint |
| Colour | Silver, silver-pink |
|---|---|
| Flash Point | 18.8°C |
| Density | 1.08 g/L (ISO: 2811) |
| Volume Solids | 30 ± 2% (ISO: 3233) |
| Volatile organic compound content | 615 (Method 24) |
| Theoretical spreading rate | 0.133-0.267 L/m2 |
| Thickness | WFT 133–267 µm |
| Dry film | 40–80 µm |
(dry film 80 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1.5 h | 1 h | 40 min | 30 min |
| Hard Dry | 12 h | 10 h | 8 h | 6 h | |
| Recoat interval | At least (AC) | 12 h | 10 h | 8 h | 6 h |
| (AF) | 15 h | 12 h | 9 h | 8 h |
At most (AC)
| (AF) | 7 days 7 days 7 days 7 days |
|---|
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH |
| Airless spray: viscosity | 80 s (Ford Cup #4) |
| Nozzle | Graco719, 721 |
| Paint output pressure | 11.7-14.7Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | VINYL THINNER |
| Thinning | 0–15% by volume |
| Newbuilding | Follow the shipyard standards. Consult your CMP representative for advice. |
|---|---|
| Repair and maintenance | Remove oil and grease. Remove salts and other contaminants with high-pressure clean water, then dry |
| Fully. Remove damaged areas by abrasive blasting to at least Sa 2 (ISO 8507-1 | 2007) or with power tools |
| tool to St2 (ISO 8507-1 | 2007). |
| Rinse with water | Consult your CMP representative for advice. |
The type and degree depend on the actual condition of the material and the required performance.
Use standards consistent with the Worldwide Marine Specifications.
| Preceding coat | BANNOH 500 and other products |
|---|---|
| Subsequent coat | Various antifouling paints |
| Packaging | One-component |
Note: 1 Before applying the subsequent coat, if the surface is contaminated by dust or dirt, first clean the surface with fresh water or by other methods.
2 Density and volatile organic compound content are theoretically calculated without thinner. Various values are determined according to paints of different colours.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.