2419K ECO SWAN Water-borne Epoxy Ester Paint is a water-borne coating. ECO SWAN is a water-borne paint with good rust resistance, adhesion and other physical properties. Parameters on this page: volume solids 50 ± 2% (ISO: 3233), dry film thickness 80–100 µm, theoretical spreading rate 0.16–0.2 L/m². Comparable models from the same brand: 1050 NZ PRIMER S zinc-free epoxy shop primer, 200 GALVANITE No.200 PRIMER epoxy galvanized steel primer, 400 GALVANITE No.400 PRIMER epoxy polyamide resin primer.
Parameter source: CMP original technical data sheet (TDS) \"2419K ECO SWAN Water-borne Epoxy Ester Paint\"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 50 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 80–100 µm |
| Theoretical Spreading Rate | 0.16-0.2 L/m2 |
| VOC | 86.0 g/L (Method 24) |
| Density / Specific Gravity | 1.44 g/mL (ISO: 2811) |
| Number of Components | One-component |
| Thinner | Clean water |
| Colour / Appearance | White, other specified colours |
| Drying Time | 30 min |
ECO SWAN is a water-borne paint with good rust resistance, adhesion and other physical properties. It provides a safer, pollution-free working environment.
SWAN HB is suitable for protection of superstructures, engine rooms, and similar areas.
| Type | Water-borne epoxy ester paint |
|---|---|
| Use | Used as an anti-corrosive primer and topcoat on ships and steel structures. |
| Colour | White, other specified colours |
|---|---|
| Flash Point | °C |
| Density | 1.44 g/mL (ISO: 2811) |
| Volume Solids | 50 ± 2% (ISO: 3233) |
| Volatile organic compound content | 86.0 g/L (Method 24) |
| Theoretical spreading rate | 0.16-0.2 L/m2 |
| Thickness | WFT 160-200 µm; DFT 80-100 µm |
(dry film 80 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 2 h | 1.5 h | 1 h | 30 min |
| Hard Dry | 14 h | 12 h | 8 h | 6 h | |
| Recoat interval | At least | 14 h | 12 h | 8 h | 6 h |
At most
| Application method | Airless spray, air spray, brush |
|---|---|
| Weather: temperature | Minimum 5 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 3-4 Pa.S |
| Nozzle | Graco515, 617, 719 |
| Paint output pressure | 10.7-13.8 Mpa |
| Spray gun speed | 70–90 cm/s |
| Thinner | Clean water |
| Thinning | 0-2% by volume |
| Preceding coat | CERABOND,EPICON ZINC RICH PRIMER B2 |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1 Ventilation facilitates water evaporation, film drying, and reaction.
2 The remaining paint after use must be tightly covered to prevent skinning.
3 Paint shall not be stored in environments below 5°C or above 40°C.
4 Do not mix with other water-borne or pigmented paints.
5 Density, volume solids, and VOC content are theoretical calculated values on a solvent-free basis.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.