Ceilcote 242 Flakeline Vinyl Ester Glass Flake Coating belongs to glass flake coatings, vinyl ester system. Ceilcote 242 Flakeline can be used in many applications in the power, mining and chemical industries where coatings with excellent chemical resistance are required. Ceilcote 242 Flakeline is a glass flake-filled vinyl ester resin coating with excellent resistance to organic and inorganic acid solutions and many aliphatic solvents. To control environmental conditions, dehumidification, air conditioning and/or heating equipment may be required. Parameters on this page: volume solids 100% reactive, dry film thickness 375–625 µm (15–25 mils), theoretical spreading rate 1.89 m²/L.
Parameter source: AKZONOBEL original technical data sheet (TDS) "Ceilcote 242 Flakeline Vinyl Ester Glass Flake Coating"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 100% active |
|---|---|
| Dry Film Thickness | 375–625 µm (15–25 mil) |
| Theoretical Spreading Rate | 1.89 m²/L |
| VOC | 2.61 lb/gal (313 g/L) US EPA Method 24 17… |
| Density / Specific Gravity | 1.22 kg/L (10.2 lb/gal) |
| Number of Components | Two-component |
| Thinner | Must not be thinned |
| Mixing Ratio | 1 L Part A : 20 ml Part B (1 gal Part… |
| Gloss | N/A |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Ceilcote 242 Flakeline is a glass flake-filled vinyl ester resin coating with excellent resistance to organic and inorganic acid solutions and many aliphatic solvents.
It has excellent chemical resistance and can be quickly put into service.
Used for coating tanks and steel structures with appropriate primer, concrete trenches, pits, dikes and secondary containment. Ceilcote 242 Flakeline can also be used as a chemical-resistant floor coating and applied to FGD (flue gas desulfurization) seawater absorbers and clean gas ducts.
Ceilcote 242 Flakeline can also be applied as a component of other Ceilcote systems over appropriate base coats.
Ceilcote 242 Flakeline can be used in many applications in the power, mining and chemical industries where coatings with excellent chemical resistance are required.
CEILCOTE Colour Grey, Off-white 242 FLAKELINE
| Gloss | N/A |
|---|---|
| Volume Solids | 100% active |
| Typical thickness | DFT 375–625 µm (15–25 mil) corresponds to WFT 441–735 µm (17.6–29.4 mil) per coat |
| Practical Spreading Rate | At a dry film thickness of 450 µm and 85% volume solids, the theoretical spreading rate is 1.89 m²/L. At 18 mil dry film thickness and 85% volume solids, the theoretical spreading rate is 76 ft²/US gal. (For more details, see the 'Product Characteristics' section.) |
| Application Methods | Suitable for airless spray, roller, brush. Drying time; self-recoat interval |
| Temperature | Surface Dry | Hard Dry | Minimum | Maximum |
| 10°C (50°F) | 5 h | 24 h | 12 h¹ | 28 days |
| 15°C (59°F) | 4 h | 16 h | 8 h¹ | 28 days |
| 25°C (77°F) | 2 h | 4.5 h | 4 h¹ | 28 days |
| 35°C (95°F) | 1.5 h | 3 h | 3 h¹ | 28 days |
¹ When the surface temperature exceeds 35 °C (95 °F) or the surface is exposed to sunlight, recoat as soon as the coating is hard enough to walk on, to avoid intercoat adhesion problems.
| Flash point (typical) | Component A 32 °C (90 °F); Component B 77 °C (171 °F); mixed 32 °C (90 °F) |
|---|---|
| Product weight | 1.22 kg/L (10.2 lb/gal) |
| Volatile Organic Compounds | 2.61 lb/gal (313 g/L) US EPA Method 24 176 g/kg EC Solvent Emissions Directive content (Council Directive 2010/75/EU) 0.83 lb/gal (99 g/L) SCAQMD Method 304-91 Coating hazard GB 30981.2-S-Pb≤1000-NC complies with GB 30981.2-2025. For more detailed information, see the "Product Characteristics" section. |
All surfaces to be coated must be clean, dry and free of contamination. Before application, all surfaces must be assessed and prepared in accordance with ISO 8504:2000. Remove any oil and grease by solvent cleaning in accordance with SSPC-SP1.
For steel substrates in immersion, humid or high-temperature service, apply this product over a suitably primed surface blast cleaned to Sa 3 (ISO 8501-1:2007), SSPC-SP5 or NACE No.1. For dry or fume environments, blast cleaning to Sa 2½ (ISO 8501-1:2007), SSPC-SP10 or NACE No.2 is appropriate. Surface roughness must be at least 75 µm (3 mils).
The concrete substrate must be well cured before flooring, lining or coating application. Refer to the concrete surface preparation guide for further information.
The surface shall be coated with Ceilcote 380 primer at a wet film thickness of 50–125 µm (2–5 mil).
| Mixing | Ceilcote 242 Flakeline must be mixed and applied according to the detailed application instructions of the subsequent system. |
|---|
This product is supplied in two containers forming one unit. Mix the two components in the specified ratio in one operation. Once mixed, use within the specified pot life.
(1) Stir the base (Component A) with a power mixer.
(2) Mix all of the curing agent (Component B) with the base (Component A) and stir thoroughly with a power mixer.
Do not mix more paint than can be used within the recommended pot life.
| Mixing ratio | 1 L Part A : 20 ml Part B (1 gal Part A : 2½ fl oz Part B) |
|---|
| Pot life | 10°C (50°F) | 15°C (59°F) | 25°C (77°F) | 35°C (95°F) |
| 60 min | 50 min | 40 min |
| Suitable for airless spray | Recommended nozzle diameter 0.69–0.84 mm (27–33 mils); total paint pressure at the nozzle not less than 155 kg/cm² (2204 psi). |
|---|
| Brush | Suitable | Several coats may be required to achieve the specified film thickness. |
| Roller application | Suitable | Several coats may be required to achieve the specified film thickness. |
| Thinner | Must not be thinned |
| Cleaner | Ceilcote T-410 solvent (or International GTA203). Note: Clean all equipment immediately after use. |
|---|---|
| Interruption of work | Do not leave material in hoses, guns or spray equipment. Flush all equipment thoroughly with Ceilcote T410 / International GTA203. Use immediately after mixing; if the pot life is exceeded, discard and remix. |
Once mixed, apply until all the mixed paint is used.
| Cleaning | Clean all equipment with Ceilcote T410 / International GTA203 immediately after use. Periodically flushing spray equipment during the working day is good practice. The frequency of cleaning depends on the quantity sprayed, temperature and elapsed time, including delays. |
|---|
All surplus material and empty containers must be disposed of in accordance with local laws and regulations.
Before using the relevant Ceilcote system, read the detailed Application Guide.
Before work begins, International Paint provides a precise system for dry film thickness and number of coats.
Although Ceilcote 242 Flakeline is 100% reactive, the actual volume solids may be lower depending on application conditions. International Paint Industrial Coatings recommends an estimated spreading rate value of 85%.
The surface temperature to be coated shall be at least 3 °C (5 °F) above the dew point. Ensure adequate ventilation during application and curing. Dehumidification, air conditioning and/or heating equipment may be required to control the environmental conditions.
At all stages of application, the surface, air and paint temperatures must be between 10 °C (50 °F) and 43 °C (110 °F).
If the recoat interval is exceeded, wipe with styrene to confirm whether recoating is possible. If the surface feels “slightly tacky”, adhesion is acceptable. If it is not softened by styrene, sweep blast or mechanically abrade the surface to obtain a matt, rough surface. Primed surfaces must be dry and free of foreign matter before lining, coating or flooring.
When applying outdoors or in sunlight, “bubbling” may occur as the surface temperature rises due to sunlight or ambient temperature. This can cause bubbles or pinholes in the applied flooring, lining or coating. When this occurs, shade the surface from sunlight, and/or apply in the cooler evening or at night, so that air does not escape from the concrete during initial cure. For more detailed advice, consult the International Paint Protective Coatings division.
Following correct application procedures, Ceilcote 242 Flakeline can be returned to service after the following time intervals: 10 °C (50 °F): 48 h; 20 °C (70 °F): 24 h; 35 °C (90 °F): 16 h. Ceilcote 242 Flakeline is not intended as a decorative topcoat; colour stability is difficult to achieve.
The maximum continuous dry heat resistance temperature of Ceilcote 242 Flakeline is 177 °C (350 °F).
Ceilcote 242 Flakeline may be used as part of the following systems: Maintenance MR system — apply one coat of Ceilcote 380 Primer, then one coat of Ceilcote 6640 with reinforcing mesh, then one or more coats of Ceilcote 242 Flakeline.
Ceilline system — first apply Ceilcote 680M Primer, then apply one coat of the elastic coating Ceilcote Ceilline with reinforcing mesh, then apply one or more coats of Ceilcote 242 Flakeline.
For further application details, refer to the product data sheets of the above products.
Note: VOC values are typical and for guidance only. They may vary with colour and general production tolerances.
Although the low-molecular-weight reactive additive becomes part of the film when cured under normal ambient conditions, analysis by EPA Method 24 shows that it also affects the VOC value.
Ceilcote 242 Flakeline should be applied to suitably prepared substrates. However, it is suitable for use over the following primer: Ceilcote 380 Primer. Ceilcote 242 Flakeline may also form part of other systems, such as Ceilcote 242 Ceilline, Ceilcote 242MR. Ceilcote 242 Flakeline is normally self-recoatable.
| For further information on the industry standards, terms and abbreviations used in this datasheet, see www.international-pc.com | Refer to the following documents provided on the website: • Definitions and Abbreviations • Surface Preparation • Coating Application • Theoretical and Practical Spreading Rate • Ceilcote 242 Flakeline Application Instructions. These sections are also available as separate publications on request. |
|---|
This product is intended for professional applicators in industrial use only.
All work, including the application and use of this product, must comply with the relevant national standards, laws and regulations on safety, health and environmental protection.
During application and the subsequent drying period (for common drying times, see the product data sheet), provide adequate ventilation to keep solvent concentrations within safe limits and prevent fire and explosion. Forced ventilation is required in confined spaces. During application and drying, personal ventilation and respiratory protection (e.g. air-fed hood or suitable filter mask) must also be provided. Take the necessary measures to prevent skin and eye contact with the coating (e.g. protective clothing, gloves, goggles, mask, barrier cream).
Before use, read and follow the Material Safety Data Sheet and the Health and Safety section of the application procedure for this product (for two-component coatings, those of the base and curing agent).
If welding or cutting is performed on metal substrate previously coated with this product, dust and fumes will be released; use suitable personal protective equipment and local exhaust ventilation.
The specific safety measures depend on the application method and working environment. If these warnings or instructions are not fully understood or cannot be strictly observed, do not use the product and consult International Paint.
| Packaging Specifications | Component A | Component B | ||
| Volume | Packaging | Volume | Packaging | |
| 15 L | 14.71 L | 20 L | 0.29 L | 0.7 L |
| 4 US gal | 5 US gal | 12.5 fl oz | 1 US pint | |
For other packaging sizes, contact AkzoNobel.
| Packaging Specifications | Component A | Component B |
| 15 L | 19.71 kg | 0.39 kg |
| 4 US gal | 45.2 lb | 1 lb |
| Shelf life | Store for 6 months at 20 °C (68 °F). Inspection is required thereafter. Store in a dry, cool environment, away from heat and ignition sources. During storage and transport, the temperature of the Ceilcote 242 Flakeline initiator must not exceed 30 °C (90 °F). Refrigeration is recommended. Part A and Part B should be stored separately. |
|---|
© 2026/5/26 AkzoNobel. All rights reserved.
All registered trademarks mentioned in this publication are licensed to or owned by AkzoNobel.
www.international-pc.com
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.
The factory item numbers of Ceilcote 242 Flakeline Vinyl Ester Glass Flake are as follows.Item No.is the most accurate form when ordering;Colour/colour codecorresponds to the actual colour (RAL, GSB are colour chart codes);Packaging SpecificationsFactory complete-set specification format. Colors not listed may be ordered against the colour card.
| Item No. | Colour / colour code | Packaging Specifications |
|---|---|---|
| NCA009 | Grey | 15.44 L |
This model has a total of1item numbers, all listed on this page; colours outside the table (including special colours and bulk packaging) can be confirmed by phone, delivery dates are advised according to the factory's current production schedule and stock. In the packaging specification, the "+" indicates the complete-set notation for two-component products (base + curing agent), subject to the factory specification; a "—" in the colour column denotes an auxiliary product, or that the item has no colour code in the factory system.