Ceilcote 282HB Flakeline Glass Flake Phenolic Vinyl Ester Coating belongs to Glass Flake, Phenolic system. Resistant to various renewable and biological raw materials and refined products (fuels), including animal fats, vegetable oils, biodiesel, ethanol, etc. Ceilcote 282HB Flakeline is a glass flake-filled phenolic vinyl ester resin coating for carbon steel substrates at high film thickness. Refrigeration is recommended to lower material temperature as much as possible to extend storage life and pot life during airless spraying. Parameters on this page: Volume Solids 93% ± 2%, Dry Film Thickness 750–1250 µm (30–50 mils), Theoretical Spreading Rate 0.93 m²/L.
Parameter source: AKZONOBEL original technical data sheet (TDS) "Ceilcote 282HB Flakeline Glass Flake Phenolic Vinyl Ester Coating"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 93% ± 2% |
|---|---|
| Dry Film Thickness | 750–1250 µm (30–50 mils) |
| Theoretical Spreading Rate | 0.93 m²/L |
| VOC | 2.26 lb/gal (271 g/L) US EPA Method 24 0.… |
| Density / Specific Gravity | 1.378 kg/L (11.5 lb/gal) |
| Number of Components | — |
| Thinner | Do not thin |
| Mixing Ratio | 51 parts : 1 part (by volume) |
| Gloss | N/A |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Ceilcote 282HB Flakeline is a glass flake-filled phenolic vinyl ester resin coating for carbon steel substrates at high film thickness. It has excellent resistance to hot flue gas environments. With or without primer, a single coat can achieve a dry film thickness of 1350 µm (54 mils). One coat can replace two coats of similar coatings. This coating is typically applied to properly prepared metal surfaces.
Designed for high-temperature flue gas desulfurization environments, including flue ducts, chimneys, dry scrubbers, bag filters, hot electrostatic precipitators, etc.
Ceilcote 282HB Flakeline has excellent chemical resistance in various environments; glass flakes provide outstanding permeability resistance.
High-build application reduces the number of applications required (single-coat application possible), shortens the construction cycle and reduces intercoat defects during recoating.
Resistant to various renewable and biological raw materials and refined products (fuels), including animal fats, vegetable oils, biodiesel, ethanol, etc.
Provides good protection against various fatty acids at elevated temperatures.
CEILCOTE Colour Grey, Off-white 282HB FLAKELINE
| Gloss | N/A |
|---|---|
| Volume Solids | 93% ± 2% |
| Typical thickness | Dry film thickness 750–1250 µm (30–50 mils) corresponds to wet film thickness 806–1344 µm (32.2–53.8 mils) |
| Theoretical Spreading Rate | At 1000 µm dry film thickness and the stated volume solids, 0.93 m²/L; at 40 mils dry film thickness and the stated volume solids, 37 ft²/US gal |
| Practical Spreading Rate | Allow appropriate loss factor. Spreading rate will vary with substrate and environmental conditions. |
For actual spreading rate, refer to the Application Guide.
| Application Methods | Suitable for airless spray. Drying time: recommended topcoat overcoating interval |
|---|
| Temperature | Surface Dry | Hard Dry | Minimum | Maximum |
| 10°C (50°F) | 90 min | 3 h | 4 h | 28 days¹ |
| 25°C (77°F) | 60 min | 2 h | 28 days¹ | |
| 40°C (104°F) | 15 min | 45 min | 60 min | 28 days¹ |
¹ Surfaces in direct sunlight must be recoated within 4 hours.
| Flash point (typical) | Component A 31 °C (88 °F); Component B 56 °C (133 °F); Mixed 31 °C (88 °F) |
|---|---|
| Product weight | 1.378 kg/L (11.5 lb/gal) |
| Volatile Organic Compounds | 2.26 lb/gal (271 g/L) US EPA Method 24; 0.53 lb/gal (64 g/L) ASTM D2369. For more details, see the "Product Characteristics" section. |
All surfaces to be coated shall be clean, dry and free from contamination. Prior to lining application, all surfaces shall be assessed and treated in accordance with 8504:2000.
Oil and grease shall be cleaned and removed in accordance with SSPC-SP1.
For steel substrates under immersion, intermittent splash or spillage conditions, blast to SSPC SP5 "White Metal" grade, or NACE 1, ISO 8503-1 Sa3 grade. Minimum roughness shall reach 100 µm (4 mils). If Ceilcote 282HB Flakeline requires a primer, 50–125 µm (2–5 mils) of Ceilcote 370HT or Ceilcote 380 is recommended.
For service at 80 °C and above, Ceilcote 370HT is required and shall be the only primer used.
| Mixing | This product is supplied in two containers forming one unit. Mix the two components in the specified ratio in one operation. Once mixed, use within the specified pot life. |
|---|
(1) Stir the base (Component A) with a power mixer.
(2) Mix all of the curing agent (Component B) with the base (Component A) and stir thoroughly with a power mixer.
| Mixing ratio | 51 parts : 1 part (by volume) |
|---|
| Pot life | 10°C (50°F) | 25°C (77°F) | 40°C (104°F) |
| 90 min | 45 min | 5 min |
| Suitable for airless spray | Recommended nozzle diameter 0.9–1.09 mm (35–43 thou); total paint pressure at nozzle not less than 155 kg/cm² (2204 psi) |
|---|---|
| Air Spray | Not applicable (with pressure pot) |
| Air spray (conventional) | N/A |
| Brush | Applicable — for small-area repair only |
| Roller application | N/A |
| Thinner | Do not thin |
| Cleaner | Ceilcote T-410 Solvent or MEK |
| Interruption of work | Do not leave paint in hoses, spray guns or spray equipment. Flush all equipment thoroughly with T-410 solvent. Mixed paint should not be re-sealed. If work is interrupted for a long period, use freshly mixed paint when work resumes. |
| Cleaning | Clean all equipment with T-410 solvent immediately after use. The frequency of cleaning depends on the quantity sprayed, temperature and time, including all interruptions. |
Surplus paint and empty containers must be disposed of in accordance with the relevant regional regulations.
Before using the relevant Ceilcote system, read the detailed Application Guide.
This data sheet provides general usage guidance for Ceilcote 282HB Flakeline. Specific project requirements will depend on final operating conditions. For storage and handling of Ceilcote 282HB Flakeline, consult International Protective Coatings.
Detailed project coating specifications provided by International Protective Coatings must be followed at all times.
Application of Ceilcote 282HB Flakeline shall be performed by the coating contractor using personnel trained in the appropriate application procedures. It is strongly recommended that both site supervisors and applicators attend the Ceilcote Application Training Course.
Higher temperatures reduce shelf life. The product, with the curing agent not added and properly sealed, has a shelf life of 3 months at 25 °C (77 °F). Do not store in sunlight. Refrigeration is recommended to keep the material temperature as low as possible, thereby extending the shelf life and the pot life during airless spray. Note that the material temperature rises during mixing. The recommended storage temperature range is 8–19 °C (46–66 °F).
Airless spray is recommended for Ceilcote 282HB Flakeline; brush application requires multiple coats to achieve the required film thickness and is suitable for small areas or areas not suitable for spraying. Brush application will alter surface smoothness.
For optimal performance, a single coat of Ceilcote 282HB Flakeline can achieve a dry film thickness of 750 to 1250 µm (30 to 50 mils). This product shall not be thinned; adding thinner will severely affect curing.
The temperature of the surface to be coated must be at least 3 °C (5 °F) above the dew point. Relative humidity during application and curing shall not exceed 80%. Below 10 °C (50 °F), the product will not cure adequately. For ideal performance, the ambient curing temperature should be above 10 °C (50 °F). Dehumidification, air conditioning and/or heating equipment may be necessary to control environmental conditions.
Application shall not proceed when substrate temperature exceeds 43 °C (110 °F). If temperature is briefly below 10 °C (50 °F), consult an International Protective Coatings representative.
If the recoating interval is exceeded, wipe with styrene to confirm whether recoating is possible. If the surface feels "slightly tacky", adhesion is acceptable. If not softened by styrene, the surface must be sweep-blasted or mechanically abraded to obtain a matt, rough surface. Primed surfaces must be dry and free from foreign matter prior to lining, coating or flooring application. When surface temperature exceeds 43 °C (110 °F) or surfaces are exposed to direct sunlight, recoating should be carried out immediately after hard dry to avoid intercoat adhesion problems. Surfaces in direct sunlight must be recoated within 4 hours.
The maximum continuous dry heat resistance of Ceilcote 282HB Flakeline is 204 °C (400 °F).
For extreme temperatures in specific environments, consult International Protective Coatings. This product is not a dedicated topcoat, so colour stability cannot be guaranteed.
Although the low-molecular-weight reactive additive becomes part of the film when cured under normal ambient conditions, analysis by EPA Method 24 shows that it also affects the VOC value.
Ceilcote 282HB Flakeline can be used with many Ceilcote primers, linings or coatings. Refer to the technical specification and Application Guide.
The following primers can be used with Ceilcote 282HB Flakeline: Ceilcote 370HT Primer, Ceilcote 380 Primer. The following topcoats are recommended for use with Ceilcote 282HB Flakeline: Ceilcote 222GF Flakeline, Ceilcote 222LSE Flakeline, Ceilcote 282 Flakeline TC, Ceilcote 282AR Flakeline
| For further information on the industry standards, terms and abbreviations used in this datasheet, see www.international-pc.com | Found in the following documents provided on the website: • Definitions and abbreviations • Surface preparation • Coating application • Theoretical and practical spreading rate • Ceilcote 282HB Flakeline application guide. These sections are also available as separate publications upon request. |
|---|
This product must be applied at the production site by professional applicators in accordance with the recommendations in this manual, the Material Safety Data Sheet and the instructions on the container label. Do not use this product without first reviewing the Material Safety Data Sheet (MSDS) that International Paint provides for its customers.
All work related to the application and use of this product must be carried out in accordance with the relevant national health, safety and environmental standards and regulations.
If welding or flame cutting is required on metal coated with this product, dust and fumes will be generated; use appropriate personal protective equipment and adequate local ventilation.
If in doubt about the suitability of this product for the intended use, consult AkzoNobel for further advice.
| Packaging Specifications | Component A | Component B | ||
| Volume | Packaging | Volume | Packaging | |
| 4 US gal | 5 US gal | 0.1 US gal | 0.13 US gal | |
| 25 US gal | 30 US gal | 0.57 US gal | 1 US gal | |
For other packaging sizes, contact AkzoNobel.
| Packaging Specifications | Component A | Component B |
| 25 US gal | 326.1 lb | 5.8 lb |
| 4 US gal | 49.3 lb | 0.8 lb |
| Shelf life | Store for 6 months at 20 °C (68 °F). Thereafter inspection is required. Store in a dry, cool environment, away from heat and ignition sources. |
|---|
The information given in this product data sheet is not exhaustive. Anyone who uses, for any purpose, any product other than those specifically recommended in this data sheet without first obtaining our written confirmation does so at their own risk as regards the suitability of the product for the intended purpose. Although to the best of our knowledge all advice or statements given about the product (whether in this data sheet or otherwise) are correct, we cannot control the quality or condition of the substrate, nor the many factors affecting the use and application of the product. Accordingly, unless we specifically agree otherwise in writing, we accept no liability, to the maximum extent permitted by law, for any product performance problem arising, or for any loss or damage caused by use of the product. We hereby disclaim any warranty or representation, express or implied, arising by operation of law or otherwise, including but not limited to any implied warranty of merchantability or fitness for a particular purpose. All products supplied and all technical guidance provided are subject to our standard terms and conditions of sale. You should obtain a copy of this document and read it carefully. The information contained in this product data sheet may be amended at any time in the light of experience and of our product development policy. Before using the product, it is the customer's responsibility to check with the local representative that the data sheet in their possession is the latest version.
This product data sheet is available on www.international-marine.com or www.international-pc.com and should be identical to this copy. If the version on the website differs from this one, the version on the website shall prevail.
©2022/11/18 AkzoNobel. All rights reserved.
www.international-pc.com
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.