Korepox Top Coat-ET6572 fresh water tank coating is a topcoat. Parameters on this page: volume solids around 66% (determined to ISO 3233), dry film thickness 125 µm, theoretical spreading rate 6.6 m²/L/100 µm. Comparable products from the same brand: Korabor Enamel RT546-FLUORESCENT RED heavy-duty topcoat, Korepox Top Coat-ET6572 fresh water tank coating, Koramel Enamel LT313 alkyd topcoat.
Data source: KCC original Technical Data Sheet (TDS), "Korepox Top Coat-ET6572 Fresh Water Tank Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | approx. 66% |
|---|---|
| Dry Film Thickness | 125 µm |
| Theoretical Spreading Rate | 6.6 m²/L /100 µm |
| VOC | — |
| Density / Specific Gravity | 1.3–1.5 kg/L (mixed, depending on colour) |
| Number of Components | Two-component |
| Thinner | 024 maximum 10% (by volume) |
| Colour / Appearance | Flat, white (1000), pale yellow (3305) |
| Packaging Specifications | 18 L pack (ET6572PTA: 9 L, ET6572PTB: 9 L) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
ET6572 is a two-component polyamide-cured epoxy resin-based high-build high-solids topcoat, designed for fresh water tanks. Complies with FDA regulation, section 175.300, and can directly contact food and be used in fresh water tanks.
As a topcoat for fresh water tanks and swimming pools.
| Appearance and colour | Flat, white (1000), pale yellow (3305) |
|---|---|
| density | Mixture, depending on colour, approx. 1.3–1.5 |
| Volume Solids | approx. 66% (determined per ISO 3233) |
| Theoretical Spreading Rate | On smooth surfaces, 5.28 m²/L at dry film thickness 125 µm |
| Flash Point | Base (ET6572PTA): 53 °C (closed cup); hardener (ET6572PTB): 48 °C (closed cup) |
*Before coating, remove all oil, grease, dust and other contaminants from the surface to be coated. *Steel: blast clean to Sa 2.5 or power tool clean to St 3.
Korepox Primer EP6172 or according to the coating specification.
Brush, roller or spray (air or airless) application. Airless spray: nozzle tip size 431.8–635.0 µm (0.017–0.025 in); spray pressure 18.0–36.5 MPa; fan 60°. *Use an airless spray machine with a compression ratio above 66:1.
Base (ET6572PTA) : Hardener (ET6572PTB) = 1 : 1 (by volume). Mix the two components completely in the specified ratio before application.
Thinner 024 maximum 10% (by volume). Do not thin the two components separately; only thin the mixture.
The application surface should be completely clean and dry, the ambient temperature should be 10–40 °C, and the relative humidity must not exceed 85%. The surface temperature should be at least 3 °C above the dew point to avoid condensation.
Dry film thickness: 125 µm. The theoretical dry film thickness varies with the use and location.
| Substrate temperature | 5°C | 20°C | 30°C |
|---|---|---|---|
| Touch dry | 12 h | 2 h | |
| Hard Dry | 48 h | 16 h | 10 h |
In accordance with the coating specification.
At 20 °C, 3 h.
At 20 °C, minimum 8 hours, maximum 11 days.
Continuous: 93 °C (non-immersion areas); intermittent: 121 °C (non-immersion areas).
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 18 L pack (ET6572PTA: 9 L, ET6572PTB: 9 L) |
Protect skin and eyes from direct contact with liquid coating, and avoid prolonged breathing of solvent vapours. Ensure adequate ventilation; keep away from sparks and open flames. Date of issue: 2010-06-01.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.