Korepox Holding Primer EP1700 Epoxy Primer is an epoxy coating used as a primer. Parameters on this page: volume solids approx. 50% (determined according to ISO 3233), dry film thickness 50 µm, theoretical spreading rate 5.0 m²/L/100 µm. Comparable products of the same brand and type: KOREPOX EH2350 High-build Epoxy Primer, KOREPOX EH2350 Epoxy Primer, Korepox Holding Primer EP1700 Epoxy Primer.
Parameter source: KCC original technical data sheet (TDS) "Korepox Holding Primer EP1700 Epoxy Primer"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 50% |
|---|---|
| Dry Film Thickness | 50 µm |
| Theoretical Spreading Rate | 5.0 m²/L per 100 µm |
| VOC | 490 g/L |
| Density / Specific Gravity | 1.3–1.5 kg/L (after mixing) |
| Number of Components | Two-component |
| Colour / Appearance | Flat, bright blue |
| Packaging Specifications | 16L(EP1700-A: 12.8L, EP1700-B: 3.2L) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EP1700 is a two-component polyamide-cured epoxy primer used to prevent corrosion on the interior and exterior of blast-cleaned steel, curing to form a hard, highly anti-corrosive coating. This product complies with U.S. Food and Drug Administration (FDA) Regulation Section 175.300 and may be used in direct contact with food products and in fresh water tanks.
Used as a temporary primer for fresh water tanks.
| Appearance and colour | Flat, bright blue |
|---|---|
| Volume solids | Approx. 50% (measured per ISO 3233) |
| Volatile Organic Compounds | 490g/L |
| Theoretical Spreading Rate | On smooth surfaces, 10.0 m²/L at a dry film thickness of 50 µm |
| density | After mixing, approx. 1.3–1.5 |
| Flash Point | Base (EP1700-A): 15 °C/59 °F (closed cup); Hardener (EP1700-B): 15 °C/59 °F (closed cup) |
Remove all oil, grease, dust and other contaminants from the surface to be coated before application. Steel: blast clean to Sa2.5 or power tool clean to St3.
The application and curing temperature shall be above 5 °C/41 °F. The surface to be coated shall be completely clean and dry; the relative humidity shall not exceed 85%, and the surface temperature shall be at least 2.7 °C (5 °F) above the dew point to avoid condensation.
Base (EP1700-A): Hardener (EP1700-B) = 4:1 (by volume). Mix in the specified ratio before application and stir thoroughly with a power mixer.
6 h at 20 °C/68 °F.
Dry film thickness 50 µm.
| Substrate Temperature | 5°C/41℉ | 20°C/68℉ | 30°C/86℉ |
|---|---|---|---|
| Touch Dry | 3 h | 30 min | |
| Hard Dry | 28 h | 4 h | 3 h |
Continuous: 93 °C/200 °F (non-immersion areas); intermittent: 121 °C/250 °F (non-immersion areas).
| Shelf life | EP1700-A (Base): 12 months; EP1700-B (Hardener): 24 months |
|---|---|
| Standard packaging sizes | 16L(EP1700-A: 12.8L, EP1700-B: 3.2L) |
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.