Korepox H.B. EH2560 Epoxy belongs to Epoxy. Parameters on this page: volume solids approx. 50% (according to ISO 3233), dry film thickness 100 µm, theoretical spreading rate 5.0 m²/L/100 µm. Comparable products of the same brand and type: KOREPOX EH2350 modified high-solids epoxy, KOREPOX EP174 epoxy wear-resistant coating, Korepox H.B. EH2560 Epoxy.
Parameter source: KCC original technical data sheet (TDS) "Korepox H.B. EH2560 Epoxy"; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | Approx. 50% |
|---|---|
| Dry Film Thickness | 100 µm |
| Theoretical Spreading Rate | 5.0 m²/L per 100 µm |
| VOC | Maximum 434 g/L |
| Density / Specific Gravity | Approx. 1.27 kg/L (after mixing) |
| Number of Components | Two-component |
| Colour / Appearance | Flat. Bright aluminium, bright yellow-aluminium |
| Packaging Specifications | 18L(EH2560-A: 15.0L, EH2560-B: 3.0L) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
EH2560 is a two-component vinyl-modified epoxy resin-based anticorrosive and sealing coating that forms a tough, high-build film with good seawater resistance, and therefore exhibits excellent compatibility with a variety of coatings (epoxy, polyurethane, chlorinated rubber, acrylic and self-polishing copolymer antifouling types).
Can be used as a multi-purpose repair coating for the outer hull of marine vessels. No tar exudation into subsequent coats.
| Appearance and colour | Flat. Bright aluminium, bright yellow-aluminium |
|---|---|
| Volume Solids | Approx. 50% (according to ISO 3233) |
| VOC | Maximum 434 g/L (according to ISO 3251) |
| Theoretical Spreading Rate | 5.0 m²/L at 100 µm dry film thickness on smooth surface |
| density | After mixing, approx. 1.27 |
| Flash Point | Base (EH2560-A): 38 °C/100 °F (closed cup); Hardener (EH2560-B): 38 °C/100 °F (closed cup) |
Before application, remove all oil, grease, dust and other contaminants from the surface by suitable methods such as solvent cleaning and fresh water washing.
The application and curing temperature shall be above 5 °C/41 °F. The surface to be coated shall be completely clean and dry; the relative humidity shall not exceed 85%, and the surface temperature shall be at least 2.7 °C (5 °F) above the dew point to avoid condensation.
Base:Hardener = 5:1 (by volume). Mix in the specified ratio before application and stir thoroughly with a power mixer.
6 h (20 °C/68 °F).
Dry film thickness 100 µm.
| Substrate Temperature | 5°C/41℉ | 20°C/68℉ | 30°C/86℉ |
|---|---|---|---|
| Touch dry | 1 h | ||
| Hard Dry | 24 h | 12 h | 10 h |
Continuous: 93 °C/200 °F (non-immersion areas); intermittent: 121 °C/250 °F (non-immersion areas).
| Shelf life | EH2560-A (Base): 12 months (25 °C); EH2560-B (Hardener): 24 months (25 °C) |
|---|---|
| Standard packaging sizes | 18L(EH2560-A: 15.0L, EH2560-B: 3.0L) |
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.