EgisPacific Self-polishing Antifouling Paint is an antifouling coating. Parameters on this page: volume solids approx. 62% (according to ISO 3233), dry film thickness 100–160 µm, theoretical spreading rate 6.2 m²/L/100 µm. Comparable models from the same brand: EgisPacific Self-polishing Antifouling Paint, Seablue-A/F783 Self-polishing Antifouling Paint.
Parameter source: KCC original technical data sheet (TDS) EgisPacific(HS) Self-polishing Antifouling Paint; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | approx. 62% |
|---|---|
| Dry Film Thickness | 100–160 µm |
| Theoretical Spreading Rate | 6.2 m²/L /100 µm |
| VOC | — |
| Density / Specific Gravity | approx. 2.1 kg/L |
| Number of Components | One-component |
| Flash Point | 26 °C/79 °F (closed cup) |
| Thinner | No. 002 |
| Colour / Appearance | Flat, red-brown, tan |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
The EgisPacific(HS) coating series is a high-performance antifouling paint with self-polishing properties and compliance with IMO 2003 regulations, based on a hydrolysed organic polymer as binder; it is an innovative TBT-free environmentally friendly antifouling paint that provides adequate protection for any type of ocean-going and coastal vessel without affecting the marine environment.
Areas requiring long-term protection: external hull newbuilding areas and ship repair areas (where organotin compounds are restricted or prohibited).
| Appearance and colour | Flat, red-brown, tan |
|---|---|
| density | approx. 2.1 |
| Volume Solids | approx. 62% (according to ISO 3233) |
| Theoretical Spreading Rate | On smooth surfaces, 4.96 m²/L at 125 µm dry film thickness |
| Flash Point | 26 °C/79 °F (closed cup) |
Before application, remove all oil, grease, dust and other contaminants from the surface by suitable methods such as solvent cleaning and fresh water washing.
Korabor Aluminum H.B RH248, Kovinyl Sealer VH137AL, Korepox H.B. EH2560 * Korepotar H.B. EH173(S) *
Apply by roller, brush or spray (conventional or airless). Airless spray: nozzle diameter 635–787 µm (0.025"–0.031"); nozzle pressure 20.7–24.1 MPa; fan angle 60°.
Thinner No. 002.
The surface to be coated shall be clean and dry; application shall only proceed when relative humidity does not exceed 85% and surface temperature is at least 2.7°C (5°F) above dew point; use an air gun to assist solvent evaporation.
Dry film thickness is 100–160 µm. Apply 2 or 3 successive coats in different colours; film thickness may affect drying time and recoat interval.
| Substrate Temperature | 5°C/41℉ | 20°C/68℉ | 30°C/86℉ |
|---|---|---|---|
| Touch dry | 8 h | 2 h | |
| Hard Dry | 18 h | 10 h | 6 h |
At 20°C/68°F, minimum 6 h, maximum unlimited.
| Shelf life | 12 months |
|---|---|
| Packaging Specifications | 15 L, 18 L |
Avoid skin contact and inhalation of organic solvents. In case of eye contact, rinse immediately with clean water for at least 15 min or seek medical advice. Issue date: 2011-07-01; revision date: 2019-07-25.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.