SeaQuest Endura II Three-component Foul Release Coating is an antifouling coating. As part of a complete coating system, it provides long-term protection of up to 90 months. SeaQuest Endura II is a three-component foul release coating based on advanced Elastotain® technology, using unique Flexcure™ tin-free curing technology. Parameters on this page: volume solids 75 ± 2%; dry film thickness 100–220 µm; theoretical spreading rate 7.5–3.4 m²/L.
Source: JOTUN original technical data sheet (TDS) 'SeaQuest Endura II Three-component Foul Release Coating'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 75 ± 2% |
|---|---|
| Dry Film Thickness | 100–220 µm |
| Theoretical Spreading Rate | 7.5–3.4 m²/L |
| VOC | 239 g/L (China) |
| Density / Specific Gravity | 1 kg/L |
| Number of Components | Three-component |
| Flash Point | 33 °C |
| Wet Film Thickness | 135–295 µm |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
SeaQuest Endura II
SeaQuest Endura II is a three-component foul release coating based on advanced Elastotain® technology, using unique Flexcure™ tin-free curing technology. A high-solids product that effectively controls foulant release under challenging conditions. The smooth, ultra-low-friction surface reduces hull ageing and improves hydrodynamic performance, increasing operational flexibility in changing trade environments. Recommended as a topcoat for immersed areas, applied only over approved tie coat surfaces. For the complete Jotun silicone foul release coating dry-dock application procedure, refer to TSS-TI-084.
Marine coatings:
Recommended for the underwater hull at dry-docking and for newbuilding hulls. Specially designed as a quality solution providing flexibility for ship sailing and trading. High gloss, good colour retention, providing a long-lasting aesthetic appearance. As part of a complete coating system, it provides long-term protection of up to 90 months.
Designed for ships with changing global trading environments.
Antifouling.
Complies with the IMO Antifouling Systems Convention AFS/CONF/26 and IMO MEPC.331(76)
Other certificates and approvals are available on request.
Red, black
Property Test/Standard Description
Ambient-curing
| Volume Solids | ISO 3233 | 75± 2 % |
| Flash Point | ISO 3679 Method 1 | 33 °C |
| Density | Theoretical Value | 1 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 211 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | US EPA Method 24 | 211 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 211 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 | 239 g/L |
High-temperature climate grade
| Volume Solids | ISO 3233 | 75± 2 % |
| Flash Point | ISO 3679 Method 1 | 33 °C |
| Density | Theoretical Value | 1kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 215 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 215 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 215 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 | 250 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
Typical recommended specification range
| Dry Film Thickness | 100–220 µm |
| Wet Film Thickness | 135–295 µm |
| Theoretical Spreading Rate | 7.5–3.4 m²/L |
| Dry Film Thickness | 100–220 µm |
| Wet Film Thickness | 135–295 µm |
| Theoretical Spreading Rate | 7.5–3.4 m²/L |
Surface Preparation
| Substrate | Minimum | Recommended |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Apply by airless spray. Careful handling is required to avoid overspray onto other areas. |
| Brush: | usable. Take care to achieve the specified dry film thickness. |
| Roller: |
| SeaQuest Endura II Comp A — Silicone Fouling-Release Coating Endura II, Component A | 17 parts |
| SeaQuest Endura II Comp B — Silicone Fouling-Release Coating Endura II, Component B | 0.7 parts |
| SeaQuest Endura II Comp C, Foul Release Coating Endura II Component C | 0.45 parts |
| High-temperature climate type SeaQuest Endura II Comp A, Foul Release Coating Endura II Component A | 17 parts |
| SeaQuest Endura II Comp B — Silicone Fouling-Release Coating Endura II, Component B | 0.7 parts |
| SeaQuest Endura II Comp C HC, Foul Release Coating Endura II Component C HC | 0.75 parts |
Do not add thinner.
| Cleaner | Jotun Thinner No. 10 |
|---|
When the thinner is used as a cleaning solvent, it must first comply with local regulatory requirements
| Nozzle tip size (inch/1000): | 15-23 |
| Nozzle pressure (minimum): | 210 bar/3000 psi |
| Substrate Temperature | 5 °C | 10 °C | 23 °C | 30 °C | 40 °C |
| Ambient-curing | |||||
|---|---|---|---|---|---|
| Touch Dry | 7 h | 6 h | 5 h | 4 h | 3 h |
| Dry/cured to immersion | 44 h | 36 h | 24 h | 20 h | |
| High-temperature climate grade | |||||
| Touch Dry | 5 h | 3 h | |||
| Dry/cured to immersion | 20 h | ||||
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
After application is complete, the substrate temperature must be maintained at no less than 5 °C for at least 2 hours. The minimum substrate temperature during drying/curing is 0 °C. If the temperature during drying/curing is 0 °C, the minimum immersion time is 48 hours.
Drying and curing times depend on controlled temperature and relative humidity (30–85%) and the product's average dry film thickness range.
For recoat interval guidance on rainy days, refer to TSS-TI-084. If very high humidity or rain occurs after applying SeaQuest Endura II, the curing process and minimum immersion time are expected to be extended. Assess the coating surface accordingly.
For wet-on-wet application guidance, refer to TSS-TI-084
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|
Dry/cured to immersion: the minimum time before the coating can be permanently immersed in sea water.
| Paint temperature | 23 °C | 30 °C | 40 °C |
| Ambient-curing | |||
|---|---|---|---|
| Pot life, high-temperature climate type | 45 min | 20 min | |
| Pot Life | 1.5 h | 1 h | 30 min |
The flexible fouling-release coating is applied over the tie-coat:
Safeguard FRC PE II, Safeguard FRC S Silicone Low-surface-energy Tie Coat S (6B7)
Foul release coatings are normally mechanically weaker than traditional self-polishing coatings, so mechanical abrasion should be avoided after application.
| Volume | Container Size |
| (L) | |
SeaQuest Endura II Comp A 17/20, Foul Release Coating Endura II Component A. SeaQuest Endura II Comp B 0.7/1, Foul Release Coating Endura II Component B. SeaQuest Endura II Comp C 0.45/1, Foul Release Coating Endura II Component C. High-temperature climate type: SeaQuest Endura II Comp A 17/20, Foul Release Coating Endura II Component A. SeaQuest Endura II Comp B 0.7/1, Foul Release Coating Endura II Component B. SeaQuest Endura II Comp C HC 0.75/1, Foul Release Coating Endura II Component C HC. The above packaging specifications are typical factory batch reference specifications; due to different local regulations, packaging and capacity vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| SeaQuest Endura II Comp A — Silicone Fouling-Release Coating Endura II, Component A | 24 months | ||
| SeaQuest Endura II Comp B — Silicone Fouling-Release Coating Endura II, Component B | 24 months | ||
| SeaQuest Endura II Comp C | 12 months | ||
| Organic Silicone Foul Release Coating | IEIn dCuormap | ICI | Component C HC |
| Foul Release Coating Endura II Component C HC | 12 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.