SEAQUANTUM PRO U One-component Hydrolysing Acrylic Silane Resin Antifouling Coating. Antifouling coating, acrylic coating system. Provides an optimized solution for vessels operating at various speeds and shipping rates with a primary focus on long-term hull performance and fuel savings. This antifouling effect is achieved through highly predictable and stable self-polishing characteristics, while reducing hull degradation, friction and speed loss. Parameters on this page: volume solids 58 ± 2%, dry film thickness 75–175 µm, theoretical spreading rate 7.7–3.3 m²/L.
Parameter source: JOTUN manufacturer's Technical Data Sheet (TDS) "SEAQUANTUM PRO U One-component Hydrolysing Acrylic Silane Resin Antifouling Coating"; values including spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 58 ± 2% |
|---|---|
| Dry Film Thickness | 75–175 µm |
| Theoretical Spreading Rate | 7.7–3.3 m²/L |
| VOC | 385 g/L |
| Density / Specific Gravity | 1.8 kg/L |
| Number of Components | One-component |
| Flash Point | 27 °C |
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10 |
| Wet Film Thickness | 130–300 µm |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
SeaQuantum Pro U
This is a one-component hydrolysing acrylic silane resin antifouling coating. Provides high antifouling protection, low frictional resistance and self-smoothing hull performance. This antifouling effect is achieved through highly predictable and stable self-polishing characteristics, while reducing hull degradation and lowering friction and speed loss. The initially smooth surface provides good dry-docking performance.
Complies with the requirements of AFS/CONF/26 in the IMO Anti-Fouling Systems Convention.
Marine coatings:
Recommended for underwater hulls on newbuildings and at dry-docking. Provides an optimised solution for vessels of various speeds and trading patterns where long-term hull performance and fuel savings are the primary concerns.
As part of a complete coating system, this product can provide long-term protection of up to 90 months.
Designed for worldwide and coastal trade. Recommended for contact with sea water and fresh water during outfitting of newbuildings.
Antifouling.
Complies with the IMO Antifouling Systems Convention AFS/CONF/26 and IMO MEPC.331(76)
Other certificates and approvals are available on request.
Deep red, light red
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 58± 2 % |
| Flash Point | ISO 3679 Method 1 | 27 °C |
| Density | Theoretical Value | 1.8 kg/L |
| VOC — USA / Hong Kong | US EPA Method 24 (test value) (CARB (SCM) 2007, SCAQMD Rule 1113, Hong Kong) | 385 g/L |
| VOC — EU | IED (2010/75/EU) (theoretical value) | 387 g/L |
| VOC — China | GB/T 23985-2009 (tested) | 396 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
Typical recommended specification range
| Dry Film Thickness | 75–175 µm |
| Wet Film Thickness | 130–300 µm |
| Theoretical Spreading Rate | 7.7–3.3 m²/L |
| Maximum total dry film thickness of a multi-coat antifouling system | 600 µm |
|---|
Surface Preparation
| Substrate | Minimum | Recommended |
| Coated surface | New tie coat or antifouling: remove any contamination affecting adhesion of the intermediate coat. | |
| Exceeding the maximum recoat interval may require cleaning, abrading or the use of another coating, as appropriate. | ||
| Aged antifouling coatings with a leached layer: | ||
| Rinse thoroughly with fresh water at a minimum nozzle pressure of 200 bar | Rinse thoroughly with fresh water at a minimum nozzle pressure of 340 bar | |
| remove. | ||
This product may be applied by the following methods
| Spray: | Apply by airless spray. |
| Brush: | usable. Take care to achieve the specified dry film thickness. |
| Roller: |
One-component
Stir or mix thoroughly with a power mixer before application.
| Thinner | JOTUN Thinner No. 7 / JOTUN Thinner No. 10 |
|---|
| Nozzle tip size (inch/1000): | 21-31 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | -10 °C | 0 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 5 h | 2 h | 45 min | 30 min | |
| Minimum recoat interval | 24 h | 16 h | 9 h | 7 h | 6 h |
| Dry/cured to immersion | 36 h | 24 h | 10 h | 9 h | 8 h |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
When three or more coats of antifouling are applied in rapid succession, the recommended time before immersion should be doubled.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to immersion: the minimum time before the coating can be permanently immersed in sea water.
Suitable anti-corrosive primer system. The recommended tie coat for the subsequent antifouling is:
Safeguard Universal ES Vinyl Epoxy (0QZ)
or
Safeguard Plus Vinyl Epoxy (5BP)
| Volume | Container Size | |
| (L) | ||
| Acrylic Silane Low-Friction Self-Smoothing Antifouling Coating (P) | 20 | |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Acrylic Silane Low-Friction Self-Smoothing Antifouling Coating (P) 12 months
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.