Penguard Fulfill SF Solvent-free Epoxy Putty is an epoxy coating. Industrial protective coatings: suitable as a putty forming part of a complete system exposed to a wide range of corrosive environments. It has high strength, providing excellent water resistance and higher mechanical strength than concrete. Parameters on this page: volume solids 97 ± 2%, dry film thickness 200–5000 µm, theoretical spreading rate 4.8–0.2 m²/L. Comparable products from the same brand: Balloxy HB Light Epoxy Ballast Tank Coating, Jota Armour Abrasion-resistant Epoxy Non-slip, Jotacote HF002 Universal Abrasion-resistant Epoxy HF.
Source: JOTUN original technical data sheet (TDS) "Penguard Fulfill SF Solvent-free Epoxy Putty"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 97 ± 2% |
|---|---|
| Dry Film Thickness | 200–5000 µm |
| Theoretical Spreading Rate | 4.8–0.2 m²/L |
| VOC | GB/T 23985-2009 8.3 16 g/L (China) |
| Density / Specific Gravity | 1.8 kg/L |
| Number of Components | Two-component |
| Thinner | JOTUN Thinner No. 17 |
| Mixing Ratio | 9 parts : 1 part (by weight) |
| Shelf life | 12 months : 12 months |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Penguard Fulfill SF
A two-component solvent-free epoxy putty for concrete protection. It has high strength, providing excellent water resistance and higher mechanical strength than concrete. It has excellent compatibility with epoxy sealers and subsequent coats. It is also suitable for steel structures in atmospheric environments. Suitable for suitably prepared concrete and carbon steel surfaces. Can be applied to 5 mm without sagging.
Industrial protective coatings:
Suitable as a putty forming part of a complete system exposed to a wide range of corrosive environments. Recommended for concrete cooling towers, bridges, LNG tanks, wharves and municipal buildings.
Can be applied with a trowel, putty knife or spatula.
Others
White
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 97± 2 % |
| Density | Theoretical Value | 1.8 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 16 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
Solids by weight (GB/T 1725): 99 ± 1%
Typical recommended specification range
| Dry Film Thickness | 200–5000 µm |
| Wet Film Thickness | 206–5155 µm |
| Theoretical Spreading Rate | 4.8–0.2 m²/L |
Theoretical spreading rate 2.7–0.1 m²/kg
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | Sa 2½ (ISO 8501-1) | |
| Concrete | Dry abrasive blast clean to SSPC-SP 13 / NACE No. 6. | |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Trowel | Use a trowel to achieve the specified thickness and smoothness. |
|---|
| JOTUN Universal Solvent-Free Epoxy Filler, Component A | 9 parts |
| JOTUN Universal Solvent-Free Epoxy Filler, Component B | 1 part |
| Manual application |
Mixing:
Stir thoroughly with a power stirrer at the correct mixing ratio, until a colour-uniform paint material is obtained before application.
| Thinner | JOTUN Thinner No. 17 |
|---|
In China, the cleaning solvent must comply with GB 38508-2020
| Substrate Temperature | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 5 h | 3 h | 2 h | |
| Walk-on Dry | 48 h | 33 h | 14 h | 6 h |
| Minimum recoat interval | 48 h | 33 h | 14 h | 6 h |
| Dry/cured to service | 21 days | 14 days | 7 days | 3 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 75 min |
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy |
| Subsequent coat: | Epoxy, modified epoxy |
| JOTUN Universal Solvent-Free Epoxy Filler, Component A | Weight 13.5 kg | Container size (L) 10 |
| JOTUN Universal Solvent-Free Epoxy Filler, Component B | 1.5 kg | 3 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| JOTUN Universal Solvent-Free Epoxy Filler, Component A | 12 months |
| JOTUN Universal Solvent-Free Epoxy Filler, Component B | 12 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.