Jotamastic 87 Aluminium low-surface-preparation epoxy abrasion-resistant aluminium-pigment coating belongs to epoxy coatings. Industrial protective coatings field: recommended for offshore environments, including splash zones, refineries, power stations, bridges, buildings, mining equipment and general structural steel. In atmospheric and immersion environments it can be used as primer, intermediate coat, topcoat or a single-coat system. Parameters on this page: volume solids 87 ± 2%, dry film thickness 150–300 µm, theoretical spreading rate 5.8–2.9 m²/L. Comparable products of the same brand and type: Balloxy HB Light epoxy ballast water tank coating, Jota Armour high-strength abrasion-resistant epoxy anti-slip coating, Jotacote HF002 general-purpose abrasion-resistant epoxy coating HF.
Parameter source: JOTUN manufacturer's Technical Data Sheet (TDS) "Jotamastic 87 Aluminium Surface-Tolerant Abrasion-resistant Epoxy Aluminium Pigment Paint"; values such as spreading rate are converted from TDS parameters and are for product selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 87 ± 2% |
|---|---|
| Dry Film Thickness | 150–300 µm |
| Theoretical Spreading Rate | 5.8–2.9 m²/L |
| VOC | 209 g/L (US) |
| Density / Specific Gravity | 1.5 kg/L |
| Number of Components | Two-component |
| Flash Point | 40 °C |
| Thinner | JOTUN Thinner No. 17 |
| Mixing Ratio | 5.5 parts : 1 part : 3.7 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Jotamastic 87 Aluminium
This is a two-component, polyamine-cured, surface-tolerant epoxy coating. It is a high-build product featuring surface tolerance and high solids content. It contains aluminium pigment, which improves protective performance. It is specifically designed for areas where ideal surface preparation cannot be achieved or is not required. It provides long-term corrosion protection in highly corrosive environments. It can be used as a primer, intermediate coat, topcoat, or single-coat system in atmospheric and immersion environments. It is suitable for properly prepared carbon steel and aged painted surfaces. It can be applied at surface temperatures below 0°C.
General:
Mainly for maintenance and repair.
Marine coatings:
Hull shell, exterior and interior areas, including ballast tanks.
Industrial protective coatings:
Recommended for offshore environments, including splash zones, refineries, power stations, bridges, buildings, mining equipment and general structural steel.
Others
It holds a Class 1 low flame-spread certificate tested according to BS 476, Part 7, 1971, Warrington Fire Research, Naval Eng. Standard 713: Issue 3.
Grain certificate issued by the Newcastle (UK) occupational health authority. Other certificates and approvals are available on request.
Jotamastic 87 — Surface-Tolerant Epoxy Abrasion-Resistant (332)
Jotamastic 87 GF — Surface-Tolerant Epoxy Abrasion-Resistant Glass Flake (336)
For the different products in this series, refer to the respective technical data sheets
Aluminium, aluminium red
Property Test/Standard Description
Ambient-curing
| Volume Solids | ISO 3233 | 87± 2 % |
| Gloss (GU 60°) | ISO 2813 | Semi-gloss (35–70) |
| Flash Point | ISO 3679 Method 1 | 40 °C |
| Density | Theoretical Value | 1.5 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 209 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 209 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 209 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 | 155 g/L |
Winter grade
| Volume Solids | ISO 3233 | 77± 2 % |
| Flash Point | ISO 3679 Method 1 | 31 °C |
| Density | Theoretical Value | 1.4kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | Calculation | 246 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | Calculation | 246 g/L |
| EU | European Paint Directive 2004/42/CE | Calculation | 246 g/L |
| China | GB 30981-2020 Limit of harmful substances of industrial protective coatings | GB/T 23985-2009 8.3 | 194 g/L |
The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 150–300 µm |
| Wet Film Thickness | 170–345 µm |
| Theoretical Spreading Rate | 5.8–2.9 m²/L |
| Dry Film Thickness | 150–250 µm |
| Wet Film Thickness | 195–325 µm |
| Theoretical Spreading Rate | 5.1–3.1 m²/L |
The recommended surface preparation provides optimum properties including adhesion, corrosion resistance, heat resistance and chemical resistance.
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 2 (ISO 8501-1) | Sa 2 (ISO 8501-1) |
| Shop-primed Steel | Clean, dry and intact shop primer (compliant with ISO 12944-4 clause 5.4). | |
| Coated surface | A clean, dry and sound compatible primer. | |
This product may be applied by the following methods
| Spray: | Apply by airless spray (5–10% dilution). | |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. | |
| Roller: | Suitable for small areas. | Not recommended for the first primer coat. Take care to achieve the specified dry film thickness. |
| Surface-tolerant Abrasion-resistant Epoxy Aluminium, Component A | 5.5 parts |
| Surface-tolerant Abrasion-resistant Epoxy, Component B | 1 part |
| Surface-tolerant Abrasion-resistant Epoxy Aluminium, Component A | 3.7 parts |
| Surface-tolerant Abrasion-resistant Epoxy, Component B (winter grade) | 1 part |
| Thinner | JOTUN Thinner No. 17 |
|---|
In China, the cleaning solvent must comply with GB 38508-2020
| Nozzle tip size (inch/1000): | 19-25 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
Substrate temperature -5 °C 0 °C 5 °C 10 °C 23 °C 40 °C Ambient-curing
| Touch Dry | 8 h | 4 h | 2 h |
| Walk-on Dry | 24 h | 10 h | 4 h |
| Minimum recoat interval | 24 h | 10 h | 4 h |
| Dry/cured to service | 14 days | 7 days | 2 days |
| Touch Dry | 24 h | 18 h | 12 h | 6 h | 2.5 h |
| Walk-on Dry | 80 h | 44 h | 26 h | 16 h | 6 h |
| Minimum recoat interval | 80 h | 44 h | 26 h | 16 h | 6 h |
| Dry/cured to service | 21 days | 14 days | 7 days | 3 days | 2 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Ambient-curing | |
|---|---|
| Induction Time | 10 min |
| Pot Life | 1.5 h |
| Winter grade | |
| Pot Life | 1 h |
Temperature
| Drying, atmospheric | Continuous 120 °C | Peak - |
| Immersed, sea water | 50 °C | 60 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Note: this coating can withstand different immersion temperatures, depending on the specific chemical and whether immersion is continuous or intermittent. Heat resistance is affected by the coating system as a whole. When used with other coatings, ensure that all coatings in the system have similar heat resistance.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Epoxy shop primer, inorganic zinc silicate shop primer, zinc epoxy, epoxy, modified epoxy, inorganic zinc silicate |
| Subsequent coat: | Polyurethane, epoxy, acrylic, vinyl epoxy |
| Volume | Container Size | |
| (L) | ||
| Surface-tolerant Abrasion-resistant Epoxy Aluminium, Component A | 14.7 | 20 |
| Surface-tolerant Abrasion-resistant Epoxy, Component B | 2.7 | 3 |
| Surface-tolerant Abrasion-resistant Epoxy, Component B (winter grade) | 4 | 5 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
| Surface-tolerant Abrasion-resistant Epoxy Aluminium, Component A | 48 months |
| Surface-tolerant Abrasion-resistant Epoxy, Component B | 48 months |
| Surface-tolerant Abrasion-resistant Epoxy, Component B (winter grade) | 36 months |
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Data is subject to the manufacturer's latest version; in all cases the manufacturer's latest TDS prevails.