Jotacote Universal F60 Epoxy F60 is an epoxy coating. This product is recommended for most areas of properly prepared substrates in industrial new construction, major maintenance and new shipbuilding. Jotacote Universal F60 provides excellent outfitting performance and enhanced protection on uninsulated surfaces over a wide operating temperature range (especially -196 °C to 200 °C). Parameters on this page: volume solids 60 ± 2%, dry film thickness 50–300 µm, theoretical spreading rate 12–2 m²/L.
Parameter source: JOTUN original technical data sheet (TDS) 'Jotacote Universal F60 Epoxy F60'; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% |
|---|---|
| Dry Film Thickness | 50–300 µm |
| Theoretical Spreading Rate | 12–2 m²/L |
| VOC | 364 g/L (China) |
| Density / Specific Gravity | 1.4 kg/L |
| Number of Components | Two-component |
| Flash Point | 26 °C |
| Thinner | Jotun Thinner No. 17 |
| Mixing Ratio | 4 parts : 1 part (by volume) |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Jotacote Universal F60
Jotacote Universal F60 is a general-purpose primer designed to provide reliable anticorrosive protection in atmospheric and immersion environments. It is a two-component polyamine-cured pure epoxy coating suitable for year-round all-weather use where fast drying is required. Jotacote Universal F60 provides excellent outfitting performance and enhanced protection on uninsulated surfaces over a wide operating temperature range (especially -196 °C to 200 °C). Previously sold under the name Jotacote F60; the formulation remains unchanged.
Suitable for steel structures exposed to atmospheric corrosion and immersed conditions. Recommended for most areas of properly prepared substrates in new industrial construction, major maintenance projects and newbuildings. Abrasive blasting is recommended to achieve optimum adhesion and durability. Passed PSPC crossover testing and suitable for use over various shop primers.
Others
Pre-qualified according to NORSOK M-501 in selected coating systems. As a primer in specific coating systems, its performance has been tested according to ISO 12944 and meets requirements up to corrosivity category CX.
Certified per IMO Res.215(82) for ballast tanks to PSPC standard; certified per IMO Res.288(87) for crude oil tanks to PSPC standard; certified compliant with the low flame-spread requirements of the IMO 2010 FTP Code. For details, consult your JOTUN representative.
Other certificates and approvals are available on request.
Grey, red, white, aluminium, aluminium red, bronze. Due to differences in pigment heat stability, slight colour change may occur when the coating is heated. Note that such colour change does not affect coating performance.
| Property | Test / Standard | Description |
| Volume Solids | ISO 3233 | 60± 2 % |
| Gloss (GU 60°) | ISO 2813 | Matt (0–35) |
| Flash Point | ISO 3679 Method 1 | 26 °C |
| Density | Theoretical Value | 1.4 kg/L |
| Region | Regulations | Test / Standard | VOC Value |
| US | CARB(SCM)2020 / SCAQMD rule 1113 | US EPA Method 24 | 366 g/L |
| Hong Kong | Air Pollution Control (VOC) Regulation | 366 g/L | |
| EU | European Paint Directive 2004/42/CE | Calculation | 399 g/L |
| China | Mandatory national standard of China | GB 30981.2-2025 | 364 g/L |
Coating hazards GB 30981.2-S-Pb≤1000-NC. The data listed are based on factory batch production and may vary slightly with colour.
| Gloss description | According to JOTUN's definition of functional coatings |
|---|
Typical recommended specification range
| Dry Film Thickness | 50–300 µm |
| Wet Film Thickness | 85–500 µm |
| Theoretical Spreading Rate | 12–2 m²/L |
Surface Preparation
| Substrate | Minimum | Recommended |
| Carbon Steel | St 2 (ISO 8501-1) | Sa 2½ (ISO 8501-1) |
| Stainless steel | The surface should be blasted with a non-metallic abrasive, | “Blast clean using an approved non-metallic abrasive |
| hand- or machine-sanded using abrasive paper or fibre discs, | to produce a sharp angular surface profile.” |
to produce scratch marks on the surface.
| Aluminium | The surface should be blasted with a non-metallic abrasive, | “Blast clean using an approved non-metallic abrasive |
| hand- or machine-sanded using abrasive paper or fibre discs, | to produce a sharp angular surface profile.” |
| Galvanised steel | The surface shall be kept clean and dry and free from zinc salts | Sweep-blast with non-metallic abrasive to produce a clean, rough and uniform surface. |
| Shop-primed Steel | Dry, clean, intact shop primer | Sweep blast or abrasive blast clean at least 70% of the area to Sa 2 (ISO 8501-1) |
| Coated surface | A clean, dry and sound compatible primer. | Sa 2½ (ISO 8501-1) |
| Composite | The surface must be roughened by hand or machine to produce a rough surface | |
| Concrete | Maximum humidity 5%. | Curing time of at least 4 weeks. Maximum moisture 5%. Seal with |
| For existing concrete surfaces, use sanding, needle gun and mechanical grinding wheel | Closed-circuit blasting, diamond grinding and other suitable methods | |
| grinding etc. for mechanical treatment | to treat the surrounding concrete surface to remove laitance. | |
The recommended surface preparation provides optimum properties including adhesion, corrosion resistance, heat resistance and chemical resistance.
This product may be applied by the following methods
| Spray: | Apply by airless spray. | |
| Brush: | Recommended for touch-up and small-area application. Take care to achieve the specified dry film thickness. | |
| Roller: | Suitable for small areas. | Not recommended for the first primer coat. Take care to achieve the specified dry film thickness. |
| Jotacote Universal F60 Comp A — General-Purpose Abrasion-Resistant Epoxy F60, Component A | 4 parts |
| Jotacote Universal F60 Comp B — General-Purpose Abrasion-Resistant Epoxy F60, Component B | 1 part |
| Thinner | Jotun Thinner No. 17 |
|---|
| Nozzle tip size (inch/1000): | 19-31 |
| Nozzle pressure (minimum): | 150 bar/2100 psi |
| Substrate Temperature | -10 °C | -5 °C | 0 °C | 5 °C | 10 °C | 23 °C | 40 °C |
| Touch Dry | 36 h | 13 h | 10 h | 6 h | 4 h | 2 h | 1 h |
| Walk-on Dry | 72 h | 28 h | 24 h | 19 h | 10 h | 3 h | 2 h |
| Minimum recoat interval | 22 h | 18 h | 10 h | 5 h | 3 h | 2 h | |
| Dry/cured to immersion | 10 days | 7 days | 4 days | 3 days | 2 days | 1 day | 12 h |
| Dry/cured to service | 14 days | 12 days | 10 days | 7 days | 3 days |
For the maximum recoat interval, refer to the Application Guide (AG) for this product.
Drying and curing times are determined based on temperature and relative humidity below 85%, with dry film thickness within the average range.
| Touch Dry | The state at which light finger pressure leaves no mark or stickiness. |
|---|---|
| Walk-on Dry | The minimum time after which the coating allows normal foot traffic without leaving permanent footprints, marks or other physical damage. |
Minimum recoat interval after drying: the recommended minimum interval before applying the next coat.
Dry/cured to immersion: the minimum time before the coating can be permanently immersed in sea water.
Dry/cured to service: the minimum time before the coating can be permanently exposed to a specific environment/medium.
| Paint temperature | 23 °C |
| Pot Life | 8 h |
Temperature
| Continuous | Peak | |
| Drying, atmospheric | 200°C | |
| Immersed, sea water | 60 °C | 70 °C |
| Immersed, crude oil | 80 °C | 90 °C |
Withstands peak temperatures for a maximum of one hour.
At the above temperatures, protective performance is unaffected, but appearance may be affected.
Note: this coating can withstand different immersion temperatures, depending on the specific chemical and whether immersion is continuous or intermittent. Heat resistance is affected by the coating system as a whole. When used with other coatings, ensure that all coatings in the system have similar heat resistance.
Depending on the actual exposure conditions in service, this product may be used with various primers and topcoats. Some reference systems are listed below. For specific systems, contact JOTUN.
| Previous coat: | Inorganic zinc silicate shop primer, epoxy |
| Subsequent coat: | Acrylic, alkyd, epoxy, modified epoxy, polyurethane, polysiloxane, vinyl epoxy |
| Volume | Container Size | |
| (L) | ||
| Jotacote Universal F60 Comp A — General-Purpose Abrasion-Resistant Epoxy F60, Component A | 16 | 20 |
| Jotacote Universal F60 Comp B — General-Purpose Abrasion-Resistant Epoxy F60, Component B | 4 | 5 |
The packaging sizes above are typical reference sizes for factory batch production. Due to regional regulatory differences, packaging sizes and capacities may vary by region.
Store in accordance with national regulations. Keep containers in a dry, cool, well-ventilated place away from heat and sources of ignition. Keep containers tightly closed. Handle with care.
Jotacote Universal F60 Comp A 24 months Universal Abrasion-resistant Epoxy F60 Component A Jotacote Universal F60 Comp B 24 months Universal Abrasion-resistant Epoxy F60 Component B
In some markets, the stated shelf life may be shortened to comply with local legal requirements. The above is the minimum shelf life; thereafter, testing is required to confirm quality remains acceptable.
For professional use only. Applicators and workers must be trained, experienced, capable and equipped to mix, stir and apply the coating correctly in accordance with JOTUN's technical documents. Applicators and workers must wear appropriate personal protective equipment when using this product. This guidance is provided based on current product knowledge. Any proposed modification to suit site conditions must be approved by the responsible JOTUN representative before use.
Read the safety warnings on the container packaging. Use in well-ventilated conditions. Avoid inhaling spray mist and avoid skin contact. In case of accidental splashes on skin, wash immediately with a suitable cleaner, soap and water. In case of eye contact, rinse thoroughly with water and seek medical attention immediately.
When used primarily as a primer or antifouling coating, products may show slight colour variation from batch to batch. Such products, and epoxy products used as topcoats, may chalk when exposed to sunlight.
Gloss and colour retention of topcoats depend on the colour type, the surrounding environment such as temperature and UV intensity, application quality and product type. Contact your local JOTUN office for further information.
The information in this datasheet is based entirely on knowledge gained in our laboratory and in practice. JOTUN products are regarded as semi-finished products, and their use is generally beyond our control. JOTUN therefore guarantees only the quality of the product itself. To comply with local regulations, the product may be adjusted, and we reserve the right to modify the datasheet without further notice.
Users should consult JOTUN for specific guidance on the suitability of the product for their requirements and applications.
In case of any discrepancy between language versions, the English (UK) version shall prevail.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.