9114 SEAJET 034 Tin-free Self-polishing Antifouling Paint is an antifouling coating. Its good antifouling performance comes from a highly active polymer that ensures high biocide effectiveness and release. Parameters on this page: volume solids 40 ± 2%; dry film thickness 50–100 µm; theoretical spreading rate 0.124–0.248 L/m². Comparable products from the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling Paint, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling Paint, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling Paint.
Source: CMP original technical data sheet (TDS) '9114 SEAJET 034 Tin-free Self-polishing Antifouling Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 40 ± 2% |
|---|---|
| Dry Film Thickness | 50–100 µm |
| Theoretical Spreading Rate | 0.124-0.248 L/m2 |
| VOC | 512 g/L |
| Density / Specific Gravity | 1.23 g/mL |
| Number of Components | One-component |
| Flash Point | 24°C |
| Thinner | SEAJET THINNER A |
| Colour / Appearance | Bright white, bright blue, bright black, bright red |
SEAJET 034 is a tin-free self-polishing antifouling paint based on a special highly hydrolysing polymer.
Good antifouling performance derives from the highly active polymer, which ensures high efficacy and release of the biocide.
Provides long-term antifouling protection through a controlled hydrolysis maintaining surface activity.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | An antifouling paint for the bottoms of GRP, aluminium and steel boats |
| Colour | Bright white, bright blue, bright black, bright red |
|---|---|
| Flash Point | 24°C |
| Density | 1.23 g/mL |
| Volume Solids | 40 ± 2% |
| Volatile organic compound content | 512 g/L |
| Theoretical spreading rate | 0.124-0.248 L/m2 |
| Wet Film Thickness | 124–248 µm |
| Dry Film Thickness | 50–100 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 6 h | 5 h | 4 h | 3 h | |
| Recoat interval | At least | 8 h | 7 h | 6 h | 5 h |
| At most | - | - | |||
| Dry-to-launch time | At least | 16 h | 12 h | 10 h | 8 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 90 s (Ford #4) |
| Nozzle | Graco 619, 625 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | SEAJET THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | SEAJET 015, VYNIL AC-HB, FRP PRIMER, etc. |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. VOC content, density and volume solids are theoretical values calculated for a representative colour formulation (bright white) without thinner. Values vary with colour formulation.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.