9110 SEAJET 033 Tin-free Self-polishing Antifouling is an antifouling. The proprietary dissolution technology of the special resin structure ensures long-term antifouling performance. Parameters on this page: volume solids 48 ± 2%, dry film thickness 50–100 µm, theoretical spreading rate 0.105–0.21 L/m². Comparable products from the same brand: 4010B SEATENDER 7 Tin-free Self-polishing Antifouling, 5843A SEAFLO NEO SL Tin-free Self-polishing Antifouling, 5843H SEAFLO NEO SL Z Tin-free Self-polishing Antifouling.
Source: CMP original technical data sheet (TDS) "9110 SEAJET 033 Tin-free Self-polishing Antifouling"; spreading rate and other values are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 48 ± 2% |
|---|---|
| Dry Film Thickness | 50–100 µm |
| Theoretical Spreading Rate | 0.105-0.21 L/m2 |
| VOC | 454 g/L |
| Density / Specific Gravity | 1.64 g/mL |
| Number of Components | One-component |
| Flash Point | 30°C |
| Thinner | SEAJET THINNER A |
| Colour / Appearance | Red, blue, black, shark white |
SEAJET 033 is a tin-free self-polishing antifouling providing long-term resistance to marine organisms.
The unique dissolution technology of the special resin structure ensures long-term antifouling performance.
| Type | Tin-free self-polishing antifouling |
|---|---|
| Use | An antifouling for the bottoms of FRP vessels |
| Colour | Red, blue, black, shark white |
|---|---|
| Flash Point | 30°C |
| Density | 1.64 g/mL |
| Volume Solids | 48 ± 2% |
| Volatile organic compound content | 454 g/L |
| Theoretical spreading rate | 0.105-0.21 L/m2 |
| Wet Film Thickness | 105–210 µm |
| Dry Film Thickness | 50–100 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 3 h | 2 h | 1 h | 30 min |
| Hard Dry | 12 h | 7 h | 5 h | 4 h | |
| Recoat interval | At least | 12 h | 7 h | 5 h | 4 h |
| At most | - | - | |||
| Dry-to-launch time | At least | 24 h | 16 h | 12 h | 8 h |
| Application method | Airless spray, brush, roller |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% RH; steel temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 90 s (Ford #4) |
| Nozzle | Graco 619, 625 |
| Paint output pressure | 14.7-17.7 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | SEAJET THINNER A |
| Thinning | 0–5% by volume |
| Preceding coat | SEAJET 015, RAVAX AC-HB, FRP PRIMER, etc. |
| Subsequent coat | - |
| Packaging | One-component |
Note: 1. VOC content, density and volume solids are theoretical calculated values based on a representative colour formulation (red) without thinner. Values differ for different colour formulations.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.