8033 SILICON HR Silicone Resin Heat-resistant Paint belongs to heat-resistant paints, silicone paint system. SILICON HR is a silicone heat-resistant coating composed of silicone resin and heat-resistant pigments. Parameters on this page: volume solids 39 ± 2% (ISO: 3233), dry film thickness 15–25 µm, theoretical spreading rate 0.038–0.064 L/m². Comparable models from the same brand: 8033B SILICON HR BLACK Silicone Resin Heat-resistant Paint, 8034 SILICON HR SILVER Silicone Heat-resistant Aluminium Paint, 8032 SILICON HR PRIMER Silicone Resin Heat-resistant Primer.
Parameter source: CMP original technical data sheet (TDS) “8033 SILICON HR Silicone Resin Heat-resistant Paint”; values such as spreading rate are converted from TDS parameters and are for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 39 ± 2% (ISO: 3233) |
|---|---|
| Dry Film Thickness | 15–25 µm |
| Theoretical Spreading Rate | 0.038-0.064 L/m2 |
| VOC | 551 g/L (Method 24) |
| Density / Specific Gravity | 1.32 g/mL (ISO: 2811) |
| Number of Components | Two-component |
| Thinner | SILICON THINNER A |
| Mixing Ratio | Base : accelerator = 100:1.42 (by volume) |
| Colour / Appearance | White, red-brown, light colours |
SILICON HR is a silicone heat-resistant coating based on silicone resin and heat-resistant pigments.
| It has the following advantages | 1. High heat resistance (up to 700 °C) 2. High weathering resistance 3. Good application properties 4. High adhesion |
|---|
| Type | Silicone Resin Heat-Resistant Coating |
|---|---|
| Use | May be used as a primer for boilers and engine cylinders; as a topcoat for exhaust pipes, radiators, oil lamps and the like |
| Mixing Ratio | Base : accelerator = 100:1.42 (by volume) |
|---|---|
| Colour | White, red-brown, light colours |
| Flash Point | Base 20 °C, accelerator 38.3 °C |
| Density | 1.32 g/mL (ISO: 2811) |
| Volume Solids | 39 ± 2% (ISO: 3233) |
| Volatile organic compound content | 551 g/L (Method 24) |
| Theoretical spreading rate | 0.038-0.064 L/m2 |
| Wet Film Thickness | 38–64 µm |
| Dry Film Thickness | 15–25 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 1 h | 50 min | 30 min | 20 min |
| Hard Dry | 7 h | 5 h | 3 h | 1 h | |
| Recoat interval | At least | 24 h | 20 h | 16 h | 10 h |
| At most | - | - | |||
| Pot life | 32 h | 28 h | 24 h | 16 h |
| Application method | Airless spray, brush |
|---|---|
| Weather: temperature | Minimum 0 °C |
| Humidity | Maximum 85% |
| Airless spray: viscosity | 25–35 s (Ford Cup #4) |
| Nozzle | Graco 415 |
| Paint output pressure | 8.8-11.8 Mpa |
| Spray gun speed | 70–100 cm/s |
| Thinner | SILICON THINNER A |
| Thinning | 7–15% by volume |
| Preceding coat | SILICON HR PRIMER |
| Subsequent coat | - |
| Packaging | Two-component |
Note: 1. The film shall be baked at 200 °C for 2 hours until fully hard dry.
2. The total film thickness of the coating system shall not exceed 150 µm.
| 3 Surface Preparation | The surface to be coated must be clean. Power brushing, detergents and solvents may be used to remove rust, oil, dust and other contaminants. |
|---|---|
| 4 Component | The mixing ratio of the accelerator (by weight) is 100:1. |
5. Density, volume solids and VOC content are theoretical calculated values without thinner.
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.