6252 GALBON S-HB PZ Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint is an inorganic zinc silicate paint. It has the following advantages: 1. excellent anti-corrosion protection 2. fast drying 3. excellent resistance to salt water and fresh water, and to oil and petroleum products. Parameters on this page: volume solids 60 ± 2%, dry film thickness 50–75 µm, theoretical spreading rate 0.083–0.125 L/m². Comparable products of the same brand: 6250 GALBON S-HB Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint, 1049A CERABOND 2000 Fast-weld Heat-resistant Inorganic Zinc Silicate Shop Primer.
Data source: CMP original Technical Data Sheet (TDS), "6252 GALBON S-HB PZ Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint"; spreading rate and other values are converted from the TDS parameters, for selection reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% |
|---|---|
| Dry Film Thickness | 50–75 µm |
| Theoretical Spreading Rate | 0.083-0.125 L/m2 |
| VOC | 423 g/L |
| Density / Specific Gravity | 2.75 g/ml |
| Number of Components | Two-component |
| Thinner | INORGANIC SHOP THINNER H |
| Mixing Ratio | Base : powder = 73:27 (by volume) |
| Colour / Appearance | Grey |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
GALBON S-HB PZ is a high-build inorganic zinc coating based on ethyl silicate and selected zinc powder.
It has the following advantages: 1. excellent anti-corrosion protection 2. fast drying 3. excellent resistance to salt water and fresh water, and to oil and petroleum products.
4. Excellent compatibility with subsequently applied organic coatings.
| Type | Alcohol-borne, self-drying, high-build inorganic zinc silicate |
|---|---|
| Use | Can be used as a primer for plants, bridges, offshore structures, pipelines and steel structures. |
| Mixing Ratio | Base : powder = 73:27 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | Base 14.5 °C, powder - °C |
| Density | 2.75 g/ml |
| Volume Solids | 60 ± 2% |
| Volatile organic compound content | 423 g/L |
| Theoretical spreading rate | 0.083-0.125 L/m2 12.0-8.0 m2/L |
| Thickness | WFT 83–125 µm |
| Dry film | 50–75 µm |
(dry film 75 µm)
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 40 min | 30 min | 20 min | 10 min |
| Hard Dry | 6 h | 5 h | 4 h | 3 h | |
| Recoat interval | At least | 72 h | 32 h | 24 h | 18 h |
| At most | - | - | |||
| Pot life | 14 h | 10 h | 7 h | 5 h | |
| Application method | Airless spray, brush (for stripe coating only) |
|---|---|
| Weather: temperature | 0 ~ 50°C |
| Humidity | 50–95% RH; steel plate temperature at least 3 °C above the dew point |
| Airless spray: viscosity | 10–12 s |
| Nozzle | Graco419, 519 |
| Paint output pressure | 9.8 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | INORGANIC SHOP THINNER H |
| Thinning | 0–7% by volume |
If applied directly to steel surfaces, surface preparation to ISO Sa2½ is required.
If applied over a shop primer coating, surface preparation to ISO St3 is required.
| Preceding coat | GALBON SP, CERABOND 2000 |
|---|---|
| Subsequent coat | Any product and/or equivalent such as inorganic zinc coatings, epoxy coatings etc. |
| Packaging | Two-component |
Note: 1 The above are spraying intervals for organic coatings. For overcoating with GALBON S-HB PZ, the spraying interval equals the hard dry time.
If applied in underwater areas, the following spraying interval should be used
| Temperature | 5°C | 10°C | 20°C | 30°C |
| Spraying interval | 14 days | 10 days | 7 days | |
2 GALBON S-HB PZ coating cannot be exposed to acid and alkali environments.
3. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
4 Stir the base with a mixer, add the powder gradually and mix slowly with a powerful mixer. Then add an appropriate amount of thinner and mix.
5. During use, stir the coating slowly and continuously to prevent zinc dust settling.
6. Do not add water. Water raises the viscosity, making it difficult to use.
7. To avoid dry spray, keep the spray gun at a suitable distance from the substrate surface.
8. To avoid cracking, the dry film shall be kept below 150 µm (wet film 250 µm). 9. When the humidity is below 50%, a longer curing time is required.
10. A mist coat is required before applying the next coat.
11. To avoid dry spray at high temperatures, INORGANIC SHOP THINNER SSS is recommended as the thinner.
12 When organic topcoats are used, the dry film thickness of GALBON S-HB PZ should be controlled at 50–100 µm.
The recommended dry film thickness is 65 µm.
| 13. Mixing ratio, base | Powder = 30:70 (by weight). 14 Density and VOC content are calculated without thinner. Values may vary with colour, production process, local regulations, etc. |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.