6250 GALBON S-HB Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint is an inorganic zinc silicate coating. It has high corrosion resistance and long-term weathering resistance, as well as good oil, solvent, saltwater and fresh water resistance. Parameters on this page: volume solids 60 ± 2%; dry film thickness 50–75 µm; theoretical spreading rate 0.083–0.125 L/m². Comparable products from the same brand: 6252 GALBON S-HB PZ Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint, 1049A CERABOND 2000 Fast-welding Heat-resistant Inorganic Zinc Silicate Shop Primer.
Source: CMP original technical data sheet (TDS) '6250 GALBON S-HB Alcohol-soluble Inorganic Zinc Silicate Air-drying High-build Paint'. Spreading rate and other values converted from the TDS; for reference only.
The above content is compiled from the manufacturer's datasheet and this site's parameter tables. For selection, coating systems and lead times, pleaseContact Usfor confirmation.
This page carries the full TDS for this product, translated from the manufacturer's original document. No file download is needed; for an original-language copy, send an enquiry.
| Volume Solids | 60 ± 2% |
|---|---|
| Dry Film Thickness | 50–75 µm |
| Theoretical Spreading Rate | 0.083-0.125 L/m2 |
| VOC | 462 g/L |
| Density / Specific Gravity | 2.66 g/ml |
| Number of Components | Two-component |
| Thinner | INORGANIC SHOP THINNER H |
| Mixing Ratio | Base : powder = 7:3 (by volume) |
| Colour / Appearance | Grey |
For more Q&A on selection, application, acceptance and defect diagnosis, seeFAQsection.
GALBON S-HB is an alcohol-solution inorganic zinc coating based on ethyl silicate and selected zinc powder. It has high corrosion resistance and long-term weathering resistance, as well as good oil, solvent, saltwater and fresh water resistance. GALBON S-HB has heat resistance up to 400 °C, and one spray coat can achieve a dry film thickness of 50–100 µm. GALBON S-HB can be used as a topcoat over GALBON SP or CERABOND 2000.
| Type | Alcohol-borne, self-drying, high-build inorganic zinc silicate |
|---|---|
| Use | Can be used as a protective coating for oil tanks, solvent tanks, ballast tanks, hull exterior, decks, heated pipelines, cargo holds and other steel structures. |
| Mixing Ratio | Base : powder = 7:3 (by volume) |
|---|---|
| Colour | Grey |
| Flash Point | Base 14.5 °C, powder - °C |
| Density | 2.66 g/ml |
| Volume Solids | 60 ± 2% |
| Volatile organic compound content | 462 g/L |
| Theoretical spreading rate | 0.083-0.125 L/m2 |
| Thickness | WFT 83–125 µm |
| Dry film | 50–75 µm |
| Temperature | 5 °C | 10 °C | 20 °C | 30 °C | |
| Drying Time | Surface Dry | 40 min | 30 min | 20 min | 10 min |
| Hard Dry | 6 h | 5 h | 4 h | 3 h | |
| Recoat interval | At least | 72 h | 32 h | 24 h | 18 h |
| At most | - | - | |||
| Pot life | 14 h | 10 h | 7 h | 5 h | |
| Application method | Airless spray, brush (for stripe coating only) |
|---|---|
| Weather: temperature | 0 ~ 50°C |
| Humidity | 50-85% RH |
| Airless spray: viscosity | 10–12 s |
| Nozzle | Graco419, 519 |
| Paint output pressure | 9.8 Mpa |
| Spray gun speed | 60–80 cm/s |
| Thinner | INORGANIC SHOP THINNER H |
| Thinning | 0–7% by volume |
If applied directly to steel surfaces, surface preparation to ISO Sa2½ is required.
If applied over a shop primer coating, surface preparation to ISO St3 is required.
| Preceding coat | GALBON SP, CERABOND 2000 |
|---|---|
| Subsequent coat | Any product and/or equivalent such as inorganic zinc coatings, chlorinated rubber coatings, epoxy coatings, coal-tar epoxy coatings |
| Packaging | Two-component |
Note: 1. The above overcoating intervals apply to organic coatings and are the same as the interval for recoating GALBON S-HB once hard dry.
2. GALBON S-HB must not be exposed to acid or alkali environments.
3. Maintain ventilation from application until full cure to remove residual solvent and promote curing.
4. Stir the base with a mixer, add the powder gradually and mix slowly with a power mixer. Then add an appropriate amount of thinner and mix.
5. During use, stir the coating slowly and continuously to prevent zinc dust settling.
6. Do not add water. Water raises the viscosity, making it difficult to use.
7. To avoid dry spray, keep the spray gun at a suitable distance from the substrate surface.
8. To avoid cracking, the dry film shall be kept below 150 µm (wet film 250 µm). 9. When the humidity is below 50%, a longer curing time is required.
10. A mist coat is required before applying the next coat.
11. To avoid dry spray at high temperatures, INORGANIC SHOP THINNER SSS is recommended as the thinner.
12. When an organic topcoat is used, the dry film thickness of GALBON S-HB should be controlled at 50–100 µm.
The recommended dry film thickness is 65 µm.
| 13. Mixing ratio, base | powder = 25:75 (by weight). 14. Density and VOC content are calculated without thinner. Values may vary with colour, production process, local regulations, etc. |
|---|
Information is subject to the manufacturer's latest version; the manufacturer's latest TDS prevails.
The technical parameters on this page are taken from the product's original manufacturer technical datasheet, the copyright of which belongs to the manufacturer. If a rights holder considers the presentation inappropriate, contact us for verification and handling.
Packaging specifications and batch lead times are subject to actual availability. PleaseContact Uscontact us for project-based calculation.